Carmel Olefins IPETHENE® 214 Low Density Polyethylene  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Extrusion Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Carmel Olefins IPETHENE® 214 Low Density Polyethylene  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
IPETHENE® 214 is a general purpose low density polyethylene film extrusion grade. It contains a high level of anti-blocking and slip additives. It is BHT free. APPLICATIONS IPETHENE® 214 is mainly used to produce 35 to 100 µm films for general purpose shopping bags, Form-Fill-Seal packaging, and shrink applications.
Physical Properties Metric English Comments
Density 0.920 g/cc
0.0332 lb/in³
ISO 1183-A
Thickness 50.0 microns
1.97 mil
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 400 %
400 %
ISO 1184
Film Elongation at Break, TD 650 %
650 %
ISO 1184
Elmendorf Tear Strength MD 500 g
500 g
ISO 6283-2
Elmendorf Tear Strength TD 350 g
350 g
ISO 6283-2
Elmendorf Tear Strength, MD 10.0 g/micron
254 g/mil
ISO 6283-2
Elmendorf Tear Strength, TD 7.00 g/micron
178 g/mil
ISO 6283-2
Dart Drop 3.00 g/micron
76.2 g/mil
F50; ISO 7765-A
Dart Drop Test 150 g
0.331 lb
F50; ISO 7765-A
Film Tensile Strength at Break, MD 24.0 MPa
3480 psi
ISO 1184
Film Tensile Strength at Break, TD 19.0 MPa
2760 psi
ISO 1184
Optical Properties Metric English Comments
Haze 8.0 %
8.0 %
ASTM D1003
Gloss 60 %
60 %
45°; ASTM D2457
Processing Properties Metric English Comments
Melt Temperature 170 °C
338 °F
Blow-up Ratio (BUR) 2.0
2.0