Lanxess Durethan® ECO BV 35 H2 900500 Nylon 6, 35% Glass Fiber

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Durethan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® ECO BV 35 H2 900500 Nylon 6, 35% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6, 35% glass fibers, injection molding, heat-ageing stabilized, contains 30% pre-consumer recycled materialInformation provided by LANXESS.
Physical Properties Metric English Comments
Specific Gravity 1.41 g/cc
1.41 g/cc
ISO 1183
Linear Mold Shrinkage, Flow 0.00050 - 0.0020 cm/cm
0.00050 - 0.0020 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
60x60x2; 290°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
60x60x2; 290°C / MT 80°C; 600 bar; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 165 MPa
23900 psi
d.a.m.; ISO 527-1, -2; 5 mm/min
Elongation at Break 3.0 %
3.0 %
d.a.m.; ISO 527-1, -2; 5 mm/min
Tensile Modulus 10.5 GPa
1520 ksi
d.a.m.; ISO 527-1, -2; 1 mm/min
Flexural Strength 260 MPa

@Strain 3.50 %
 37700 psi

@Strain 3.50 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Modulus 9.80 GPa
1420 ksi
d.a.m., 2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) <= 10.0 kJ/m²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 180-1A
10.0 kJ/m²

@Temperature 23.0 °C
 4.76 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 180-1A
Izod Impact, Unnotched (ISO) 60.0 kJ/m²

@Temperature -30.0 °C
 28.6 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 180-1U
70.0 kJ/m²

@Temperature 23.0 °C
 33.3 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 180-1U
Charpy Impact Unnotched 6.00 J/cm²

@Temperature -30.0 °C
 28.6 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 179-1eU
7.50 J/cm²

@Temperature 23.0 °C
 35.7 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 179-1eU
Charpy Impact, Notched <= 1.00 J/cm²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 179-1eA
1.10 J/cm²

@Temperature 23.0 °C
 5.23 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 179-1eA
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
10°C/min; ISO 11357-1, -3
Deflection Temperature at 0.46 MPa (66 psi) 217 °C
423 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
ISO 75-1, -2
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
280 °C
536 °F
for test specimens; ISO 294
Mold Temperature 80.0 °C
176 °F
for test specimens; ISO 294
80.0 - 120 °C
176 - 248 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 2 - 6 hour
2 - 6 hour
Moisture Content 0.030 - 0.12 %
0.030 - 0.12 %
residual; Karl Fischer Test
Descriptive Properties Value Comments
ISO Shortname ISO 1874-PA 6, GHR, 14-100, GF35