Solvay Specialty Polymers Hyflon® MFA® F1520 Perfluoropolymer

Category Polymer , Thermoplastic , Fluoropolymer , TFE/Perfluoromethylvinylether Copolymer (MFA)
Manufacturer Solvay Specialty Polymers
Trade Name Hyflon® MFA®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Hyflon® MFA® F1520 Perfluoropolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Hyflon® F is a family of MFA polymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, high flexural endurance, inherent flame resistance, low surface energy and exceptional dielectric properties. Hyflon® MFA F1520 is a low melt flow rate multi purpose resin with an exceptional stress crack resistance, continuous service temperature up to 225°C and a 100-150x10³ cycles flex-life (on a 0.3mm film, ASTM D2176).Features: Flame Retardant; Good Flexibility; High ESCR (Stress Crack Resist.); Low FlowUses: General Purpose; Wire & Cable ApplicationsAdditional Properties: Crystallization Heat - DSC 16.0 to 24.0 J/g; Flange Temperature - 370 to 400 °C; Flex Life - ASTM D2176 1.0E+5 to 1.5E+5 Cycles; Heat of Fusion - DSC 16.0 to 24.0 J/gInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 2.11 - 2.16 g/cc
0.0762 - 0.0780 lb/in³
ASTM D792
Melt Flow 1.0 - 4.0 g/10 min

@Load 5.00 kg,
Temperature 372 °C
1.0 - 4.0 g/10 min

@Load 11.0 lb,
Temperature 702 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 55 - 60
55 - 60
ASTM D2240
Tensile Strength at Break >= 30.0 MPa
>= 4350 psi
50 mm/min; ASTM D638
Elongation at Break >= 300 %
>= 300 %
50 mm/min; ASTM D638
Tensile Modulus 0.400 - 0.500 GPa
58.0 - 72.5 ksi
1.0 mm/min; ASTM D638
Izod Impact, Notched NB
NB
ASTM D256
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 120 - 200 µm/m-°C
66.7 - 111 µin/in-°F
Specific Heat Capacity 0.900 - 1.10 J/g-°C
0.215 - 0.263 BTU/lb-°F
ASTM C351
Thermal Conductivity 0.200 W/m-K

@Temperature 40.0 °C
1.39 BTU-in/hr-ft²-°F

@Temperature 104 °F
ASTM C177
Melting Point 265 - 275 °C
509 - 527 °F
DSC
Crystallization Temperature 255 - 265 °C
491 - 509 °F
Peak; ASTM D3418
Flammability, UL94 V-0
V-0
Oxygen Index 95 %
95 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+17 ohm-cm
>= 1.00e+17 ohm-cm
ASTM D257
Surface Resistance >= 1.00e+17 ohm
>= 1.00e+17 ohm
ASTM D257
Dielectric Constant 2.0

@Frequency 100000 Hz
2.0

@Frequency 100000 Hz
ASTM D150
2.0

@Frequency 50.0 Hz
2.0

@Frequency 50.0 Hz
ASTM D150
Dielectric Strength 35.0 - 40.0 kV/mm

@Thickness 1.00 mm
889 - 1020 kV/in

@Thickness 0.0394 in
ASTM D149
Dissipation Factor <= 0.00050

@Frequency 100000 Hz
<= 0.00050

@Frequency 100000 Hz
ASTM D150
<= 0.00050

@Frequency 50.0 Hz
<= 0.00050

@Frequency 50.0 Hz
ASTM D150
Processing Properties Metric English Comments
Zone 1 240 - 290 °C
464 - 554 °F
Zone 2 270 - 320 °C
518 - 608 °F
Zone 3 300 - 360 °C
572 - 680 °F
Zone 4 320 - 380 °C
608 - 716 °F
Zone 5 340 - 390 °C
644 - 734 °F
Adapter Temperature 370 - 400 °C
698 - 752 °F
Melt Temperature 400 °C
752 °F
Die Cooling Temperature 390 - 420 °C
734 - 788 °F
Descriptive Properties Value Comments
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Form Pellets
Processing Technique Extrusion Coating
RoHS Compliance RoHS Compliant