Solvay Specialty Polymers AvaSpire® AV-750 GF40 Polyaryletherketone (PAEK) (Unverified Data**)

Category	Polymer , Thermoplastic , Polyketone , Polyaryletherketone (PAEK), Glass Fiber Filled
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers AvaSpire® AV-750 GF40 Polyaryletherketone (PAEK) (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

AvaSpire AV-750 GF40 is a 40% glass reinforced polyaryletherketone (PAEK) designed to fill the marketplace need for a lower-priced PEEK (polyetheretherketone). This resin provides the typical chemical resistance expected of PEEK while maintaining excellent elevated temperature properties. The price and performance of this resin will expand the opportunities for PEEK resins especially in the area of metal replacement for corrosion control. - Natural: AvaSpire AV-750 GF40 NTInformation provided by Solvay Specialty Polymers.

Physical Properties	Metric	English	Comments
Specific Gravity	1.65 g/cc	1.65 g/cc	ASTM D792
Filler Content	40 %	40 %	Glass Fiber Reinforcement
Water Absorption	0.10 % @Time 86400 sec	0.10 % @Time 24.0 hour	ASTM D570
Viscosity	450000 cP @Shear Rate 1000 1/s, Temperature 400 °C	450000 cP @Shear Rate 1000 1/s, Temperature 752 °F	Melt; ASTM D3835
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Thickness 3.18 mm	0.0010 - 0.0030 in/in @Thickness 0.125 in	5" x 0.5" x 0.125" bars; ASTM D955
Linear Mold Shrinkage, Transverse	0.012 - 0.014 cm/cm @Thickness 3.18 mm	0.012 - 0.014 in/in @Thickness 0.125 in	5" x 0.5" x 0.125" bars; ASTM D955
Melt Flow	7.0 g/10 min @Load 2.16 kg, Temperature 380 °C	7.0 g/10 min @Load 4.76 lb, Temperature 716 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	105	105	M-Scale; ASTM D785
Tensile Strength	191 MPa	27700 psi	50 mm/min; ASTM D638
Tensile Strength, Yield	188 MPa	27300 psi	5 nm; ISO 527-2/1A/5
Elongation at Break	1.8 %	1.8 %	5.0 mm/min; ASTM D638
	1.8 %	1.8 %	ISO 527-2/1A/5
Tensile Modulus	15.1 GPa	2190 ksi	5.0 mm/min; ASTM D638
	16.7 GPa	2420 ksi	ISO 527-2/1A/1
Flexural Strength	250 MPa	36300 psi	ISO 178
	54.0 MPa @Temperature 250 °C	7830 psi @Temperature 482 °F	ASTM D790
	253 MPa @Temperature 23.0 °C	36700 psi @Temperature 73.4 °F	ASTM D790
Flexural Modulus	14.8 GPa	2150 ksi	ASTM D790
	15.4 GPa	2230 ksi	ISO 178
Compressive Strength	182 MPa	26400 psi	ASTM D695
Shear Strength	89.0 MPa	12900 psi	ASTM D732
Izod Impact, Notched	0.530 J/cm	0.993 ft-lb/in	ASTM D256
	5.90 J/cm	11.1 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	8.50 kJ/m²	4.04 ft-lb/in²	ISO 180
Izod Impact, Unnotched (ISO)	41.0 kJ/m²	19.5 ft-lb/in²	ISO 180

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	15.0 µm/m-°C @Temperature -50.0 - 50.0 °C	8.33 µin/in-°F @Temperature -58.0 - 122 °F	TMA; ASTM E831
Specific Heat Capacity	1.26 J/g-°C @Temperature 50.0 °C	0.301 BTU/lb-°F @Temperature 122 °F	DSC
	1.62 J/g-°C @Temperature 200 °C	0.387 BTU/lb-°F @Temperature 392 °F	DSC
Thermal Conductivity	0.310 W/m-K	2.15 BTU-in/hr-ft²-°F	ASTM E1530
Melting Point	345 °C	653 °F	Peak; ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi)	285 °C	545 °F	Annealed; ASTM D648
Glass Transition Temp, Tg	150 °C	302 °F	ASTM D3418
Flammability, UL94	V-1 @Thickness 0.800 mm	V-1 @Thickness 0.0315 in	UL 94
	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in	UL 94

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.80e+17 ohm-cm	1.80e+17 ohm-cm	ASTM D257
Surface Resistance	>= 1.90e+17 ohm	>= 1.90e+17 ohm	ASTM D257
Dielectric Constant	3.66 @Frequency 1.00e+6 Hz	3.66 @Frequency 1.00e+6 Hz	ASTM D150
	3.68 @Frequency 60.0 Hz	3.68 @Frequency 60.0 Hz	ASTM D150
	3.69 @Frequency 1000 Hz	3.69 @Frequency 1000 Hz	ASTM D150
Dielectric Strength	19.0 kV/mm	483 kV/in	ASTM D149
Dissipation Factor	0.0010 @Frequency 1000 Hz	0.0010 @Frequency 1000 Hz	ASTM D150
	0.0020 @Frequency 60.0 Hz	0.0020 @Frequency 60.0 Hz	ASTM D150
	0.0030 @Frequency 1.00e+6 Hz	0.0030 @Frequency 1.00e+6 Hz	ASTM D150

Processing Properties	Metric	English
Melt Temperature	370 - 395 °C	698 - 743 °F
Mold Temperature	175 - 210 °C	347 - 410 °F
Drying Temperature	150 - 175 °C	302 - 347 °F
Dry Time	2.50 - 4.00 hour	2.50 - 4.00 hour
Back Pressure	0.138 - 0.345 MPa	20.0 - 50.0 psi
Screw Speed	75 rpm	75 rpm

Descriptive Properties	Value	Comments
Appearance	Natural Color
Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Features	Flame Retardant
	Good Chemical Resistance
	Good Dimensional Stability
	High Heat Resistance
	High Stiffness
	High Strength
Forms	Pellets
Generic	PAEK
Processing Method	Injection Molding
	Machining
	Profile Extrusion
RoHS Compliance	RoHS Compliant
Screw Compression Ratio	2.0:1.0
Uses	Aircraft Applications
	Electrical/Electronic Applications
	Metal Replacement
	Seals