Lanxess Durethan® BKV 50 H EF DUS022 900116 Nylon 6, Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 50 H EF DUS022 900116 Nylon 6, Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, 50% glass fibers, injection molding, improved flowability, heat-aging stabilizedInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.57 g/cc | 1.57 g/cc | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00020 cm/cm | 0.00020 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0020 cm/cm | 0.0020 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.00070 cm/cm | 0.00070 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0070 cm/cm | 0.0070 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 128 MPa | 18600 psi | cond.; ISO 527-1, -2; 5 mm/min |
| 205 MPa | 29700 psi | d.a.m.; ISO 527-1, -2; 5 mm/min | |
| Elongation at Break | 2.3 % | 2.3 % | ISO 527-1, -2; 5 mm/min |
| 4.3 % | 4.3 % | ISO 527-1, -2; 5 mm/min | |
| Tensile Modulus | 9.50 GPa | 1380 ksi | cond.; ISO 527-1, -2; 1 mm/min |
| 16.2 GPa | 2350 ksi | d.a.m.; ISO 527-1, -2; 1 mm/min | |
| Flexural Strength | 203 MPa @Strain 4.00 % |
29400 psi @Strain 4.00 % |
cond., 2 mm/min; ISO 178-A |
| 320 MPa @Strain 2.90 % |
46400 psi @Strain 2.90 % |
d.a.m., 2 mm/min; ISO 178-A | |
| Flexural Yield Strength | 197 MPa @Strain 3.50 % |
28600 psi @Strain 3.50 % |
cond., 2 mm/min; ISO 178-A |
| Flexural Modulus | 9.70 GPa | 1410 ksi | cond., 2 mm/min; ISO 178-A |
| 15.0 GPa | 2180 ksi | d.a.m., 2 mm/min; ISO 178-A | |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 180-1A |
| 14.0 kJ/m² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 180-1A | |
| 20.0 kJ/m² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 70.0 kJ/m² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 180-1U |
| 75.0 kJ/m² @Temperature -30.0 °C |
35.7 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 180-1U | |
| 80.0 kJ/m² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 180-1U | |
| Charpy Impact Unnotched | 8.00 J/cm² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 179-1eU |
| 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 179-1eU | |
| 8.50 J/cm² @Temperature 23.0 °C |
40.4 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 179-1eU | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 179-1eA |
| 1.30 J/cm² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 179-1eA | |
| Puncture Energy | 3.60 J @Load <=124.8 kg |
2.66 ft-lb @Load <=275.2 lb |
d.a.m.; ISO 6603-2 |
| 5.80 J @Load <=128.7 kg |
4.28 ft-lb @Load <=283.7 lb |
cond.; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
5.56 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1, -3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | ISO 75-1, -2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| 280 °C | 536 °F | for test specimens; ISO 294 | |
| Mold Temperature | 80.0 °C | 176 °F | for test specimens; ISO 294 |
| 80.0 - 120 °C | 176 - 248 °F | ||
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 6 hour | 2 - 6 hour | |
| Moisture Content | 0.030 - 0.12 % | 0.030 - 0.12 % | residual; Karl Fischer Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shortname | ISO 1874-PA 6, GHR, 10-160, GF50 |
Users viewing this material also viewed the following:
- RheTech Products HP514-489 14% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, 101E Lite Oak
- Cookson Group Plaskon® SMT-B-1F Epoxy Molding Compound for PBGAs (discontinued **)
- Albis Plastics Cellulose Acetate Propionate CP800 (Base Grade), 18% Plasticizer (discontinued **)
- Solvay TECHNYL® A 218 V35 Black 34 NG PA66, 35% glass fiber, DRY
- Techmer ES HiFill® PA6/6 GB15 15% Glass Bead Filler
- Shinkong Synthetic Fibers Shinite® F102G30 PET, 30% Glass Filled, Fire Retardant, Halogen Free
- Denka VINYKON W2086 PVC, W grade for insulation, for sheaths
- Atom Adhesives AA-DUCT N02 Epoxy Adhesive
- Crucible Steel PDCQ Premium Quality High Toughness H13 Steel
- Karina 06/152-FC-LMP Blue Color Concentrate for PVC
Copyright © lookpolymers.com All Rights Reserved