Amity Thermosets ATI 172 Phenolic Molding Organic and inorganic Filler, Injection Molded

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic
Manufacturer Amity Thermosets
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Amity Thermosets ATI 172 Phenolic Molding Organic and inorganic Filler, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Characteristics:Heat resistant ( asbestos free )Good electric insulationLow shrinkageLow water absorptionMedium mechanical strengthNot suitable for high mechanical tensionColor-blackVery soft flow Applications: Heat shields Oven knobs Toaster knobsCoffee machine baseThermal insulationSwitchgear components which ought to withstand heat (200 0C), etc. Information provided by Amity Thermosets Limited
Physical Properties Metric English Comments
Density 1.45 - 1.55 g/cc
0.0524 - 0.0560 lb/in³
Molding; IS 867-1963
Apparent Bulk Density 0.670 - 0.750 g/cc
0.0242 - 0.0271 lb/in³
IS 867-1963
Water Absorption 0.25 - 0.50 %
0.25 - 0.50 %
IS 13411-1993
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
Compression specimen; IS 13411-1992
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 - 50.0 MPa
5800 - 7250 psi
5 mm/min.; IS 867-1963
Shear Strength 66.0 - 75.0 MPa
9570 - 10900 psi
IS 867-1963
Izod Impact, Notched 0.200 - 0.300 J/cm
0.375 - 0.562 ft-lb/in
IS 13411-1992
Thermal Properties Metric English Comments
Maximum Service Temperature, Air >= 200 °C
>= 392 °F
2 hours
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+11 - 3.16e+11 ohm-cm
1.00e+11 - 3.16e+11 ohm-cm
IS 3396-1979
Surface Resistance 1.00e+10 - 1.00e+11 ohm
1.00e+10 - 1.00e+11 ohm
IS 3396-1979
Dielectric Strength 5.50 - 7.50 kV/mm

@Temperature 90.0 °C
140 - 191 kV/in

@Temperature 194 °F
IS 2584-1963
Comparative Tracking Index >= 125 V
>= 125 V
2824-1975
Processing Properties Metric English Comments
Rear Barrel Temperature 65.0 - 85.0 °C
149 - 185 °F
Front Barrel Temperature 85.0 - 95.0 °C
185 - 203 °F
Nozzle Temperature <= 105 °C
<= 221 °F
Mold Temperature 160 - 180 °C
320 - 356 °F
Injection Pressure 98.0 - 196 MPa
14200 - 28400 psi
Hold Pressure 58.8 MPa
8530 psi
Cure Time 0.333 - 0.500 min
0.00556 - 0.00833 hour
per mm
Shelf Life 12.0 Month
12.0 Month
10-25°C