Polymer Property : Flexural Modulus = 15.0 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	15.0 GPa	2180 ksi
Cookson Group Plaskon® 3400FP Epoxy Molding Compound  (discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.A fast curing, reduced-stress epoxy molding compound for the encapsulation of semiconductor devices including DIPs, PLCCs, SOICs ..
Flexural Modulus	15.0 GPa	2180 ksi
Cookson Group Plaskon® SMT-B-1FX (146.801) Epoxy Molding Compound for PBGAs  (discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.An epoxy molding compound optimized specifically for PBGA applications. It is a reduced catalyst version of SMT-B-1F and provide..
Flexural Modulus	15.0 GPa	2180 ksi
Lehmann & Voss LUVOCOMÂ® 1105-7442 PEEK, with carbon fiber, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Dynamic stressed parts.High chemical resistance parts, hydrolysis resi..
Flexural Modulus	15.0 GPa	2180 ksi
Lehmann & Voss LUVOCOMÂ® 1114-8364 PAEK, with carbon fiber, PTFE, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Good friction and wear behaviour especially at increased temperatures.Electrically conduct..
Flexural Modulus	15.0 GPa	2180 ksi
Lehmann & Voss LUVOCOMÂ® 1301-7329/GY PPS, linear, with glass fiber Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.Strong, stiff parts.High continuous use and heat distortion temperature. Non flammable.High chemic..
Flexural Modulus	15.0 GPa	2180 ksi
Lehmann & Voss LUVOCOMÂ® 20-8261 Polyphthalamide, with carbon fiber, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Dynamic stressed parts at high movement velocity.Improved friction and wear..
Flexural Modulus	15.0 GPa	2180 ksi
Lehmann & Voss LUVOCOMÂ® 20-8286 Polyphthalamide, with carbon fiber, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Dynamic stressed parts at high movement velocity.Improved friction and wear..
Flexural Modulus	15.0 GPa	2180 ksi
Lehmann & Voss LUVOCOMÂ® 3/CF/30 Polyamide 6, with carbon fiber Applications: Automotive industry, textile machinery, apparatus- and precision engineering.High-strength and stiff parts; low coefficient of expansion.dynamic stressElectrically conductive, suitable..
Flexural Modulus	15.0 GPa	2180 ksi
Lehmann & Voss LUVOCOMÂ® 3/CF/30/EG Polyamide 6, with carbon fiber, extrusion grade Applications: Automotive industry, textile machinery, apparatus- and precision engineering.High-strength and stiff parts; low coefficient of expansion.dynamic stressElectrically conductive, suitable..
Flexural Modulus	15.0 GPa	2180 ksi	d.a.m., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® BKV 50 H EF DUS022 900116 Nylon 6, Glass Fiber Reinforced PA 6, 50% glass fibers, injection molding, improved flowability, heat-aging stabilizedInformation provided by LANXESS.
Flexural Modulus	15.0 GPa	2180 ksi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP KCL34A Acetal Homopolymer LNP* LUBRICOMP* KCL34A is a compound based on Acetal Homopolymer resin containing 15% PTFE, 20% Carbon Fiber. Added features of this material include: Wear Resistant, Electrically Conductive.
Flexural Modulus	15.0 GPa	2180 ksi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP KCL34A Acetal Homopolymer (Asia Pacific) LNP* Lubricomp* KCL34A is a compound based on Acetal Homopolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.
Flexural Modulus	15.0 GPa	2180 ksi	ISO 178
Solvay TECHNYLSTARâ„¢ AFX 218 V50 PA6, 50% glass filled, DRY Description TECHNYLSTARâ„¢ AFX 218 V50 is based on a patented high flow polyamide 66 resin (Technylstar), heat stabilized, reinforced with 50% of glass fiber, for injection molding. It is availab..
Flexural Modulus	15.0 GPa	2180 ksi	ISO 178
Solvay Specialty Polymers OmnixÂ® 4050 Polyamide, High Performance (HPPA) (Dry) OmnixÂ® 4050 is a 50% glass-fiber reinforced, high-performance polyamide (HPPA). It is particularly suited for replacing die-cast metal in a variety of mechanical applications and components used ..
Flexural Modulus	15.0 GPa	2180 ksi	ISO 178
Solvay Specialty Polymers OmnixÂ® 9050 Polyamide, High Performance (HPPA), 50% Glass Fiber OmnixÂ® 9050 is a 50% glass-fiber reinforced high-performance polyamide. It is hot-water moldable and intended for use in components requiring superior mechanical properties even after moisture ab..
Flexural Modulus	15.0 GPa	2180 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Verton MV00CS PP (Europe-Africa-Middle East) LNP* VERTON* MV00CS is a compound based on PP resin containing Long Glass Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Flexural Modulus	15.0 GPa	2180 ksi	ASTM D790
Plenco 7556 Phenolic, Briquette, Injection Molded PLENCO 07556 is a glass fiber reinforced novolac phenolic molding compound, with good physical strengths and heat resistance along with excellent dimensional stability. UL recognized under component..
Flexural Modulus	15.0 GPa	2180 ksi	ASTM D790
Covestro Baydur® STR/C-400 BB Polyurethane Composite SRIM Foam, 60% Glass Filled, MDI-based 2-Component Liquid System Contains directed chopped fiber preform glass.0.16 in. thickness.Information provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bay..
Flexural Modulus	>= 15.0 GPa	>= 2180 ksi	IEC 1212-2 5.2
Hippe EP GM 202 Glass Mat Reinforced Epoxy Resin - Sheet
Flexural Modulus	15.0 GPa	2180 ksi	2 mm/min; ISO 178
Eurostar Staramide RF00AES PA66/6, 50% Glass Filled, Injection Molded Staramide RF00AES is a 50% Glass Fiber Reinforced Polyamide 66/Polyamide 6 Injection Molding Resin (also known as Staramide 66 C 50V S3)Information provided by Eurostar.
Flexural Modulus	15.0 GPa	2180 ksi
Elisto THERMOSTAR® MD 130 Pattern material Densified laminated woodInformation provided by elisto
Flexural Modulus	>= 15.0 GPa	>= 2180 ksi	IEC 1212-2 5.2
Hippe EP GM 201 Glass Mat Reinforced Epoxy Resin - Sheet Used in mechanical and electrical applications. Extremely high mechanical strength at moderate temperature. Very good electrical properties under high humidity.Information provided by Hippe.
Flexural Modulus	15.0 - 20.0 GPa	2180 - 2900 ksi	Compression; ISO 178
Raschig Group RALUPOL® 8605 UP Polyester Glass fiber reinforced polyester molding compound. Resistant to hydrolysis. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU dire..
Flexural Modulus	15.0 GPa	2180 ksi	ASTM D790
LNP Lubricomp® OCL-4534 EM Polyphenylene Sulfide, Carbon Fiber Reinforced, PTFE + Silicone Lubricant  (discont Features: Good Moldability, LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP g..
Flexural Modulus	15.0 GPa	2180 ksi	ISO 178
Hexion Bakelite™ PF 4111 Phenolic Formaldehyde Resin, Improved Electrical Properties, Ammonia Free, Resistant to High Temperatures, Low Shrinkage, High Arc Resistance, UL Listed, Acetic Acid Free, Copper Adhesive Phenolic molding compound, inorganically filled, glass fiber reinforced, ammonia and acetic acid free, electrically high grade, high temperature stability, high mechanical strength, copper-adhesive,..
Flexural Modulus	15.0 GPa	2180 ksi	ASTM D790
Sumitomo Bakelite North America Epiall® 1908M-1 Short Glass Fiber Reinforced Epoxy Epiall 1908M-1 is a short glass fiber reinforced epoxy molding compound with excellent dimensional stability, good strength properties, and good electrical insulation properties.Information provided..
Flexural Modulus	15.0 GPa	2180 ksi	ASTM D790
Sumitomo Bakelite North America FM 4005 Fiberglass Reinforced Phenolic Novolac FM 4005 is a fiberglass reinforced phenolic novolac molding compound, with excellent dimensional stability and good strength at elevated temperatures. This material is compliant with the specificat..
Flexural Modulus	15.0 GPa	2180 ksi	ASTM D790
Solvay Specialty Polymers Ryton® R-4-200NA Polyphenylene Sulfide Compound  (Unverified Data**) Natural Color Polyphenylene Sulfide CompoundRyton® R-4-200NA is an advanced 40% fiberglass reinforced polyphenylene sulfide compound developed to provide high strength, fast cycles, and low mainten..
Flexural Modulus	15.0 GPa	2180 ksi	ASTM D790
LATI LARAMID G/45 45% Glass Filled Polyphthalamide (PPA) Based Compound  (Unverified Data**) Laramid compounds are based on a unique semi-crystalline engineering polymer (polyphthalamide) offering improved performance compared to traditional engineering thermoplastics at a lower cost than s..