Lanxess Durethan® BKV 230 H3.0 000000 Nylon 6-Copolymer, 30% Glass Fibers
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 230 H3.0 000000 Nylon 6-Copolymer, 30% Glass Fibers.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6-Copolymer, 30% glass fibers, injection molding, impact modified, heat-ageing stabilized
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ISO 1183 |
| Bulk Density | 0.700 g/cc | 0.0253 lb/in³ | ISO 60 |
| Moisture Absorption at Equilibrium | 1.8 % | 1.8 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 6.0 % | 6.0 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 2.00 mm |
0.0020 in/in @Thickness 0.0787 in |
Mold Temp 80°C; Melt Temp 280°C; 600 bar; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Thickness 2.00 mm |
0.0070 in/in @Thickness 0.0787 in |
Mold Temp 80°C; Melt Temp 280°C; 600 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 75.0 MPa | 10900 psi | Conditioned; ISO 527-1,-2 |
| 125 MPa | 18100 psi | ISO 527-1,-2 | |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527-1,-2 |
| 8.5 % | 8.5 % | Conditioned; ISO 527-1,-2 | |
| Tensile Modulus | 4.40 GPa | 638 ksi | Conditioned; ISO 527-1,-2 |
| 8.00 GPa | 1160 ksi | ISO 527-1,-2 | |
| Flexural Strength | 115 MPa @Strain 7.00 % |
16700 psi @Strain 7.00 % |
Conditioned; ISO 178 |
| 200 MPa @Strain 3.50 % |
29000 psi @Strain 3.50 % |
ISO 178 | |
| 205 MPa @Strain 4.30 % |
29700 psi @Strain 4.30 % |
ISO 178 | |
| Flexural Yield Strength | 90.0 MPa @Strain 3.50 % |
13100 psi @Strain 3.50 % |
Conditioned; ISO 178 |
| 200 MPa @Strain 3.50 % |
29000 psi @Strain 3.50 % |
ISO 178 | |
| Flexural Modulus | 4.10 GPa | 595 ksi | Conditioned; ISO 178 |
| 7.50 GPa | 1090 ksi | ISO 178 | |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A |
| 15.0 kJ/m² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 180-1A | |
| 20.0 kJ/m² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A | |
| 35.0 kJ/m² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 75.0 kJ/m² @Temperature 23.0 °C |
35.7 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1U |
| 80.0 kJ/m² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 180-1U | |
| 85.0 kJ/m² @Temperature -30.0 °C |
40.4 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1U | |
| 95.0 kJ/m² @Temperature 23.0 °C |
45.2 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 180-1U | |
| Charpy Impact Unnotched | 8.50 J/cm² @Temperature 23.0 °C |
40.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU |
| 8.50 J/cm² @Temperature -30.0 °C |
40.4 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179-1eU | |
| 9.50 J/cm² @Temperature -30.0 °C |
45.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eU | |
| 10.0 J/cm² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179-1eU | |
| Charpy Impact, Notched | 1.50 J/cm² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eA |
| 1.50 J/cm² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179-1eA | |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eA | |
| 4.00 J/cm² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 130 µm/m-°C | 72.2 µin/in-°F | ISO 11359-1,-2 |
| Melting Point | 213 °C | 415 °F | ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1,-2 |
| Shrinkage | 0.070 % @Temperature 120 °C, Time 14400 sec |
0.070 % @Temperature 248 °F, Time 4.00 hour |
Molding Post-shrinkage; ISO 294-4 |
| 0.15 % @Temperature 120 °C, Time 14400 sec |
0.15 % @Temperature 248 °F, Time 4.00 hour |
Molding Post-shrinkage; ISO 294-4 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | Recommended |
| 280 °C | 536 °F | Processing conditions for test specimens; ISO 294 | |
| Mold Temperature | 80.0 °C | 176 °F | Processing conditions for test specimens; ISO 294 |
| 80.0 - 100 °C | 176 - 212 °F | Recommended | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 6 hour | 2 - 6 hour | |
| Moisture Content | 0.030 - 1.12 % | 0.030 - 1.12 % | Residual; Acc. To Karl Fischer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shortname | ISO 1874-PA 6/66-HI,GHR,14-080,GF30 |
Users viewing this material also viewed the following:
- Shin-Etsu Silicones KEG-2000-30A/B Elastomer
- A. Schulman PP 984 Polypropylene Medium Impact Polypropylene
- CP-Polymer-Technik Wellamid® 6000 GVS 10/20 HWCP 10% Glass Fiber and 20% Glass Sphere Nylon 6, Heat Stabilized, Conditioned
- DuPont™ Bynel® 22E757 Modified Ethylene Acrylate
- EPICHEM Epiryl PPO V0 Polyphenylene oxide
- Epoxy Technology EPO-TEK® OE188 High Temperature Silica-Filled Epoxy
- Asahi Kasei Thermylene® P-30TC-1156 Chemically Coupled Polypropylene Compound, 30% Talc Filled
- Ashley Polymers Ashlene® 105 PBT Polyester
- American Polymers API 550 Polystyrene
Copyright © lookpolymers.com All Rights Reserved