Lanxess Durethan® BG 30 X H3.0 000000 Nylon 6, 30% Glass Fibers/Glass Spheres
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Bead Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BG 30 X H3.0 000000 Nylon 6, 30% Glass Fibers/Glass Spheres.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, 30% glass fibers/glass spheres, injection molding, heat-ageing stabilized, low tendency to warp
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.355 g/cc | 1.355 g/cc | ISO 1183 |
| Bulk Density | 0.700 g/cc | 0.0253 lb/in³ | ISO 60 |
| Moisture Absorption at Equilibrium | 2.2 % | 2.2 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 7.0 % | 7.0 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Thickness 2.00 mm |
0.0050 in/in @Thickness 0.0787 in |
Mold Temp 80°C; Melt Temp 280°C; 600 bar; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Thickness 2.00 mm |
0.0080 in/in @Thickness 0.0787 in |
Mold Temp 80°C; Melt Temp 280°C; 600 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 75.0 MPa | 10900 psi | Conditioned; ISO 2039-1 |
| 185 MPa | 26800 psi | ISO 2039-1 | |
| Tensile Strength at Break | 65.0 MPa | 9430 psi | Conditioned; ISO 527-1,-2 |
| 120 MPa | 17400 psi | ISO 527-1,-2 | |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527-1,-2 |
| 10 % | 10 % | Conditioned; ISO 527-1,-2 | |
| Tensile Modulus | 3.20 GPa | 464 ksi | Conditioned; ISO 527-1,-2 |
| 6.40 GPa | 928 ksi | ISO 527-1,-2 | |
| Flexural Strength | 100 MPa @Strain 8.00 % |
14500 psi @Strain 8.00 % |
Conditioned; ISO 178 |
| 185 MPa @Strain 5.00 % |
26800 psi @Strain 5.00 % |
ISO 178 | |
| Flexural Yield Strength | 80.0 MPa @Strain 3.50 % |
11600 psi @Strain 3.50 % |
Conditioned; ISO 178 |
| 165 MPa @Strain 3.50 % |
23900 psi @Strain 3.50 % |
ISO 178 | |
| Flexural Modulus | 2.80 GPa | 406 ksi | Conditioned; ISO 178 |
| 5.80 GPa | 841 ksi | ISO 178 | |
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A |
| <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 180-1A | |
| <= 10.0 kJ/m² @Temperature -40.0 °C |
<= 4.76 ft-lb/in² @Temperature -40.0 °F |
ISO 180-1A | |
| <= 10.0 kJ/m² @Temperature -40.0 °C |
<= 4.76 ft-lb/in² @Temperature -40.0 °F |
Conditioned; ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1U |
| 35.0 kJ/m² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1U | |
| 40.0 kJ/m² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 180-1U | |
| 80.0 kJ/m² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 180-1U | |
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eU |
| 4.50 J/cm² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU | |
| 4.50 J/cm² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179-1eU | |
| 7.50 J/cm² @Temperature 23.0 °C |
35.7 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179-1eU | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179-1eA |
| <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eA | |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eA | |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179-1eA | |
| <= 1.00 J/cm² @Temperature -40.0 °C |
<= 4.76 ft-lb/in² @Temperature -40.0 °F |
ISO 179-1eA | |
| <= 1.00 J/cm² @Temperature -40.0 °C |
<= 4.76 ft-lb/in² @Temperature -40.0 °F |
Conditioned; ISO 179-1eA | |
| Puncture Energy | 1.70 J @Load <=69.9 kg, Temperature -30.0 °C |
1.25 ft-lb @Load <=154 lb, Temperature -22.0 °F |
ISO 6603-2 |
| 2.00 J @Load <=71.5 kg, Temperature 23.0 °C |
1.48 ft-lb @Load <=158 lb, Temperature 73.4 °F |
ISO 6603-2 | |
| Tensile Creep Modulus, 1 hour | 2400 MPa | 348000 psi | Conditioned; ISO 889-1 |
| Tensile Creep Modulus, 1000 hours | 2000 MPa | 290000 psi | Conditioned; ISO 889-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1,-2 |
| Melting Point | 222 °C | 432 °F | ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1,-2 |
| Vicat Softening Point | >= 200 °C @Load 5.10 kg |
>= 392 °F @Load 11.2 lb |
120°C/h; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Glow Wire Test | 650 °C @Diameter 2.00 mm |
1200 °F @Diameter 0.0787 in |
IEC 60695-2-12 |
| Shrinkage | 0.20 % @Temperature 120 °C, Time 14400 sec |
0.20 % @Temperature 248 °F, Time 4.00 hour |
Molding Post-shrinkage; ISO 294-4 |
| 0.30 % @Temperature 120 °C, Time 14400 sec |
0.30 % @Temperature 248 °F, Time 4.00 hour |
Molding Post-shrinkage; ISO 294-4 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.5 @Frequency 100 Hz |
4.5 @Frequency 100 Hz |
IEC 60250 | |
| Dissipation Factor | 0.022 @Frequency 1.00e+6 Hz |
0.022 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 0.0265 @Frequency 100 Hz |
0.0265 @Frequency 100 Hz |
IEC 60250 | |
| Comparative Tracking Index | 375 V | 375 V | Solution A, Rating; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 °C | 536 °F | Processing conditions for test specimens; ISO 294 |
| 270 - 290 °C | 518 - 554 °F | Recommended | |
| Mold Temperature | 80.0 °C | 176 °F | Processing conditions for test specimens; ISO 294 |
| 80.0 - 120 °C | 176 - 248 °F | Recommended | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 6 hour | 2 - 6 hour | |
| Moisture Content | 0.030 - 0.12 % | 0.030 - 0.12 % | Residual; Acc. To Karl Fischer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flammability | Passed US-FMVSS302 | ISO 3795 |
| ISO Shortname | ISO 1874-PA 6,GHR,14-060, (GB+GF)30 |
Users viewing this material also viewed the following:
- Lucent Polymers PC-1410 Polycarbonate, Injection/Extrusion Grade
- Lehmann & Voss LUVOCOM® 1105/GF/20/EM/RD PEEK, with glass fiber
- Techmer ES Plaslube® J-1/30/SI/2 Nylon 66, 30% GFR, 2% Silicone
- Saint-Gobain Norton® Fluorglas® Chemfilm® DF2919 Fluoropolymer Tape
- A. Schulman POLYBATCH™ White P8550 C Concentrate Based In Polypropylene
- Eastman Tenite Butyrate 576E3720010 Clear, Trsp Cellulose Acetate Butyrate
- Dow LDPE 993I Low Density Polyethylene
- ExxonMobil Escorene™ LD 706.15 Molding Ethylene Vinyl Acetate Copolymer
- Aclo Accutech Polypropylene Copolymer CP0436W20L Wollastonite Reinforced
- Plaskolite West Optix® CP - 75 General Purpose Acrylic Resin
Copyright © lookpolymers.com All Rights Reserved