A. Schulman ComAlloy® E-12421 Reinforced High Flow Polyamide
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman ComAlloy® E-12421 Reinforced High Flow Polyamide.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 cm/cm @Thickness 3.175 mm |
0.0070 in/in @Thickness 0.1250 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 93.1 MPa | 13500 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Strength | 153 MPa | 22200 psi | ASTM D790 |
| Flexural Modulus | 4.87 GPa | 706 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm | 0.600 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.74 J/cm | 7.00 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
Users viewing this material also viewed the following:
- Huntsman AVALON® 80 ABX Thermoplastic Polyurethane
- Kinlead PT12 Adhesive Tape Grade BOPP Plain Film (thickness: 28 µm)
- SABIC Innovative Plastics Ultem 1010KM PEI (Europe-Africa-Middle East)
- Techmer ES HiFill® PA6/6 GF25 L BK 25% Glass Filled
- A. Schulman POLYPUR™ FPU 1107 Thermoplastic Polyurethane Compound
- Cossa Polimeri ESTALENE EN 10 EC Modified Polyolefin Blend
- Dow Corning SYL-OFF® C4-2109 RELEASE ADDITIVE
- 3M FM062 Indoor UL Recognized Brite Silver Polyester Label Products
- 3M Scotch-Weld™ PR Gel Plastic and Rubber Instant Adhesive
- Total Lacqrene® 6631 Impact Polystyrene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved