Lanxess Durethan® BC 600 HTS DUSXBL 900116 Nylon 6, Impact Modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BC 600 HTS DUSXBL 900116 Nylon 6, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, non-reinforced, extrusion, blow molding, impact modified, heat-aging stabilizedInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ISO 1183 |
| Moisture Absorption at Equilibrium | 2.1 % | 2.1 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 7.4 % | 7.4 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.00010 cm/cm | 0.00010 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.017 cm/cm | 0.017 in/in | 60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.014 cm/cm | 0.014 in/in | 60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | cond.; ISO 527-1, -2; 50 mm/min |
| 39.0 MPa | 5660 psi | d.a.m.; ISO 527-1, -2; 50 mm/min | |
| Elongation at Yield | 6.3 % | 6.3 % | d.a.m.; ISO 527-1, -2; 50 mm/min |
| 92 % | 92 % | cond.; ISO 527-1, -2; 50 mm/min | |
| Tensile Modulus | 0.350 GPa | 50.8 ksi | cond.; ISO 527-1, -2; 1 mm/min |
| 1.30 GPa | 189 ksi | d.a.m.; ISO 527-1, -2; 1 mm/min | |
| Flexural Strength | 15.0 MPa @Strain 8.00 % |
2180 psi @Strain 8.00 % |
cond., 2 mm/min; ISO 178-A |
| 50.0 MPa @Strain 6.00 % |
7250 psi @Strain 6.00 % |
d.a.m., 2 mm/min; ISO 178-A | |
| Flexural Yield Strength | 11.0 MPa @Strain 3.50 % |
1600 psi @Strain 3.50 % |
cond., 2 mm/min; ISO 178-A |
| 44.0 MPa @Strain 3.50 % |
6380 psi @Strain 3.50 % |
d.a.m., 2 mm/min; ISO 178-A | |
| Flexural Modulus | 0.350 GPa | 50.8 ksi | cond., 2 mm/min; ISO 178-A |
| 1.40 GPa | 203 ksi | d.a.m., 2 mm/min; ISO 178-A | |
| Izod Impact, Notched (ISO) | 70.0 kJ/m² @Temperature -30.0 °C |
33.3 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 180-1A |
| 85.0 kJ/m² @Temperature -30.0 °C |
40.4 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 180-1A | |
| 90.0 kJ/m² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 180-1A | |
| 90.0 kJ/m² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | d.a.m.; ISO 180-1U |
| NB | NB | cond.; ISO 180-1U | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
d.a.m.; ISO 179-1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
cond.; ISO 179-1eU | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
d.a.m.; ISO 179-1eU | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
cond.; ISO 179-1eU | |
| Charpy Impact, Notched | 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 179-1eA |
| 7.00 J/cm² @Temperature -30.0 °C |
33.3 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 179-1eA | |
| 10.0 J/cm² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 179-1eA | |
| 11.0 J/cm² @Temperature 23.0 °C |
52.3 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 170 µm/m-°C @Temperature 23.0 - 55.0 °C |
94.4 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| CTE, linear, Transverse to Flow | 190 µm/m-°C @Temperature 23.0 - 55.0 °C |
106 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| Melting Point | 219 °C | 426 °F | 10°C/min; ISO 11357-1, -3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 81.0 °C | 178 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-1, -2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 230 - 280 °C | 446 - 536 °F | |
| 260 °C | 500 °F | for test specimens; ISO 294 | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| 80.0 °C | 176 °F | for test specimens; ISO 294 | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 6 hour | 2 - 6 hour | |
| Moisture Content | 0.00 - 0.060 % | 0.00 - 0.060 % | residual; Karl Fischer Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shortname | ISO 1874-PA 6-HI, BHR, 14-010 |
Users viewing this material also viewed the following:
- Outokumpu 4438 High Performance Austenitic Stainless Steel
- Niche Polymer PA66GF13BK Nylon 66, 13% Glass Fiber Filled
- Kennametal Stellite Stellite® STAR cast
- LG Chemical LUPOY GN-2151F Halogen Free Modified PC, 15% Glass Fiber Reinforced, Flame Retardant, Green
- Unitika EX-1030 PA6, Dry
- CoorsTek PlasmaPure™ Alumina (nom. 99.8% Al2O3)
- Hippe PA 66 GF 30 Nylon 66 30% Glass fiber Reinforced
- DuPont Performance Polymers Zytel® FN718 NC010A Nylon 66
- Arkema Group Kynar® 1000 HDC N 118 PVDF (discontinued **)
- DuPont Performance Polymers Hypalon® 30 Chlorosulfonated Polyethylene Rubber, Mineral Filled Compound (discon
Copyright © lookpolymers.com All Rights Reserved