Polymer Property : Tensile Strength, Yield = 29.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	29.0 MPa	4210 psi	ASTM D638
NOVA Chemicals Sclair® 2907 HDPE Injection Molding Resin Features: High stiffness, maximum impact strength and toughness, good top loading capability, high surface gloss.Applications: Protective sports equipment, safety helmets, high impact custom molding..
Tensile Strength, Yield	29.0 MPa	4210 psi	50 mm/min; ISO 527
Polimeri Europa Edistir RC 600 Polystyrene Special medium impact polystyrene grade exhibiting very high gloss. This grade is designed to be used in injection moulding where an excellent surface finish is requiredApplications: Examples of ap..
Tensile Strength, Yield	29.0 MPa	4210 psi	ASTM D638
Ineos ABS Centrex® 401 AES Extrusion (discontinued **) Properties tested in transverse direction (worst case) on 125-mil (3.2 mm) extruded sheets specimens with
Tensile Strength, Yield	29.0 MPa	4210 psi	ASTM D638
Flint Hills 13T25A Random Copolymer Polypropylene Features: Excellent clarity, blush resistant and good flexural modulus. Product does not contain animal derived components.Applications: Injection Molded - Lab ware, food packaging and medical. ..
Tensile Strength, Yield	29.0 MPa	4210 psi	ASTM D638
Flint Hills P6G2N-095 Impact Copolymer Polypropylene Features: Excellent stiffness and impact resistance, nucleated, suitable for retort and hot fill applications. Product does not contain animal derived components.Applications: Blow molding, sheet/..
Tensile Strength, Yield	29.0 MPa	4210 psi	50 mm/min; ISO 527-1,-2
Inno-Comp INNOPOLÂ® CS 2-2120 20% Talc-Filled Polypropylene Block-Copolymer INNOPOLÂ® CS 2-2120 is a 20% talc-filled compound based on polypropylene block-copolymer. This grade is available in nature and custom colored form.INNOPOLÂ® CS 2-2120 is developed for producing..
Tensile Strength, Yield	29.0 MPa	4210 psi	cond.; ISO 527-1, -2; 50 mm/min
Lanxess DurethanÂ® BC 600 HTS DUSXBL 900116 Nylon 6, Impact Modified PA 6, non-reinforced, extrusion, blow molding, impact modified, heat-aging stabilizedInformation provided by LANXESS.
Tensile Strength, Yield	29.0 MPa @Strain 0.200 %, Temperature 1095 Â°C	4210 psi @Strain 0.200 %, Temperature 2003 Â°F
Haynes 214Â® alloy, hot rolled solution annealed plate 12.7 mm (1/2 in.) thick Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Yield	29.0 MPa	4210 psi	ISO 527
Iran Petrochemical (PCC) I3 HC 7260(THE) High Density Polyethylene I3 (HC 7260) is a high density polyethylene with propylene as comonomer. The product has good impact strength, good stress cracking resistance, low warping and good flow ability as well as high dens..
Tensile Strength, Yield	29.0 MPa	4210 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP 2Z004 ETFE LNP* THERMOCOMP* 2Z004 is a compound based on ETFE resin containing 20% Milled Glass.
Tensile Strength, Yield	29.0 MPa	4210 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP WH0450E PBT LNP* Thermocomp* WH0450E is a compound based on Polybutylene Terephalate resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.
Tensile Strength, Yield	29.0 MPa	4210 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP RFB44XE PA 66 (Europe-Africa-Middle East) LNP* Thermocomp* RFB44XE is a compound based on Nylon 66 resin containing Glass Fiber, Glass Bead. Added features of this material include: Easy Molding.
Tensile Strength, Yield	29.0 MPa	4210 psi
UBE UBEPOL BR15HL HIPS (n-DM =0.03 wt %) Description: UBEPOL-BR15HL is a linear type of polymer with the high solution viscosity. In case of enlarging the dispersed rubber particle size in
Tensile Strength, Yield	29.0 MPa	4210 psi	ASTM D638
UBE UBESTA® 3020IX1 Rigid Automotive Grade Nylon 12 Description: UBE UBESTA® Automotive grade Nylon 12Comments: conductive, impact modifiedInformation provided by UBE.
Tensile Strength, Yield	29.0 MPa	4210 psi	ASTM D638
A. Schulman POLYFORT™ FPP 1609 Mica Fortified Copolymer Polypropylene DescriptionPolyfort® FPP 1609 is a 10% mica fortified copolymer polypropylene product. Information provided by A. Schulman.
Tensile Strength, Yield	29.0 MPa	4210 psi	2 in/min; ASTM D638
A. Schulman PP 3475-01 Polypropylene High Melt Homopolymer Polypropylene DescriptionPolypropylene PP 3475-01 Natural is a high melt homopolymer polypropylene with consistent general purpose homopolymer characteristics. Information provided by A. Schulman.
Tensile Strength, Yield	29.0 MPa	4210 psi	ASTM D638
A. Schulman POLYFORT™ FPP 1237 CaCO3 filled homopolymer polypropylene DescriptionPolyfort® FPP 1237 is a 20% CAC03 filled homopolymer polypropylene product. Information provided by A. Schulman.
Tensile Strength, Yield	29.0 MPa	4200 psi	2" (50mm) per min; ASTM D638
Formosa Plastics Formolene® 3302B Random Copolymer Polypropylene Random Copolymer for Extrusion and Thermoforming Applications Formolene® 3302B is a low melt flow random with excellent clarity, fast cycle time and easy mold release, designed for extrusion proces..
Tensile Strength, Yield	29.0 MPa	4210 psi	ASTM D638
Total PPC M6823MZ Metallocene Isostatic Propylene Polymer TOTAL Petrochemicals Polypropylene M6823MZ is an isostatic form of copolymer polypropylene made via TOTAL Petrochemicals proprietary metallocene catalyst technology.Clarity. M6823MZ incorporates th..
Tensile Strength, Yield	29.0 MPa	4210 psi	ISO 572-2
Total PPR 7220 Random Copolymer Polypropylene, Injection Molding Total Petrochemicals PPR 7220 is a nucleated random copolymer polypropylene with a melt flow index of 10 g/10 min for the injection molding of articles with high transparency and excellent surface a..
Tensile Strength, Yield	29.0 MPa	4210 psi	ASTM D638
A. Schulman POLYFORT™ FPP 1609 Mica Fortified Copolymer Polypropylene DescriptionPolyfort® FPP 1609 is a 10% mica fortified copolymer polypropylene product. Information provided by A. Schulman.
Tensile Strength, Yield	29.0 MPa	4210 psi	ASTM D638
A. Schulman POLYFORT™ FPP 1237 CaCO3 filled homopolymer polypropylene DescriptionPolyfort® FPP 1237 is a 20% CAC03 filled homopolymer polypropylene product. Information provided by A. Schulman.
Tensile Strength, Yield	29.0 MPa	4200 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR Suprex Clay Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	29.0 MPa	4210 psi	ASTM D638
Eastman Tenite Butyrate 264A3720013 Clear, Trsp Cellulose Acetate Butyrate Plasticizer 13%. Weight loss on heating = 0.6% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p..
Tensile Strength, Yield	29.0 MPa	4200 psi	ASTM D638
ExxonMobil Paxon™ BA53-035 Blow Molding Resin (discontinued **) BA53-035 is a high molecular weight, high density polyethylene copolymer offering an outstanding combination of stiffness and toughness. The resin provides superior melt strength and impact resista..
Tensile Strength, Yield	29.0 MPa	4210 psi	ASTM D638
Ineos Nova 5711 High Impact Polystyrene (discontinued **) High flow, High impact, USP Class VIApplications: Thin wall, Medical, Housewares, ToysProperties were determined on injection molded specimens at 23°C and 50% R.H. unless otherwise specified.Inform..
Tensile Strength, Yield	29.0 MPa	4200 psi	ASTM D638
Asahi Kasei Thermofil P-40TC-2767 40% Talc Reinforced, Heat Stabilized Information provided by Asahi Thermofil
Tensile Strength, Yield	29.0 MPa	4200 psi	2" (50mm) per min; ASTM D638
Formosa Plastics Formolene® 6375N Impact Copolymer Polypropylene Impact Copolymer For High Speed Injection Molded Applications Formolene® 6375N is a very high melt flow, low impact copolymer of polypropylene. It is designed for such applications as packaging, ho..
Tensile Strength, Yield	29.0 MPa	4210 psi	At 50 mm/min; ISO 527-2
Borealis Bormed™ HE2581-PH HDPE for Healthcare Applications Bormed HE2581-PH is a high-density polyethylene intended for blow molding of products with high stiffness and very good environmental stress crack resistance (ESCR). Bormed HE2581-PH can as well be ..
Tensile Strength, Yield	29.0 MPa	4210 psi	ASTM D638
Ineos Nova 4501 Medium Impact Polystyrene (discontinued **) Good toughnessApplications: Light louvers, Injection molding applicationsProperties were determined on injection molded specimens at 23°C and 50% R.H. unless otherwise specified.Information provide..