Lanxess Durethan® AKV 30 H2.0 901510 Nylon 66, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® AKV 30 H2.0 901510 Nylon 66, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 66, injection molding-grade, 30% glass fibers, good heat-ageing resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Water Absorption | 5.5 % | 5.5 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Viscosity Test | 146 cm³/g | 146 cm³/g | Viscosity number; ISO 307, 1157, 1628 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 110 MPa | 16000 psi | Conditioned; ISO 527-1/-2 |
| 170 MPa | 24700 psi | ISO 527-1/-2 | |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 |
| 4.4 % | 4.4 % | Nominal; ISO 527-1/-2 | |
| 6.0 % | 6.0 % | Conditioned; ISO 527-1/-2 | |
| 6.7 % | 6.7 % | Nominal, Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 6.00 GPa | 870 ksi | Conditioned; ISO 527-1/-2 |
| 10.0 GPa | 1450 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| 7.50 J/cm² @Temperature 23.0 °C |
35.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| 8.50 J/cm² @Temperature 23.0 °C |
40.4 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eA | |
| <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| 1.40 J/cm² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA | |
| Impact | 835 | 835 | Puncture maximum force (N); ISO 6603-2 |
| 1161 | 1161 | Puncture maximum force, Conditioned (N); ISO 6603-2 | |
| 768 @Temperature -30.0 °C |
768 @Temperature -22.0 °F |
Puncture maximum force (N); ISO 6603-2 | |
| Puncture Energy | 2.80 J | 2.07 ft-lb | ISO 6603-2 |
| 5.40 J | 3.98 ft-lb | Conditioned; ISO 6603-2 | |
| 2.30 J @Temperature -30.0 °C |
1.70 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| 2.30 J @Temperature -30.0 °C |
1.70 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 263 °C | 505 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 135 °C | 275 °F | ISO 75-1/-2 |
| Vicat Softening Point | 230 °C | 446 °F | 50°C/h 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
IEC 60695-11-10 | |
| Oxygen Index | 23 % | 23 % | ISO 4589-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Conditioned; IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 |
| 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
IEC 60250 | |
| 12 @Frequency 100 Hz |
12 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | Conditioned; IEC 60243-1 |
| 35.0 kV/mm | 889 kV/in | IEC 60243-1 | |
| Dissipation Factor | 0.012 @Frequency 100 Hz |
0.012 @Frequency 100 Hz |
IEC 60250 |
| 0.019 @Frequency 1.00e+6 Hz |
0.019 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 0.080 @Frequency 1.00e+6 Hz |
0.080 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 0.27 @Frequency 100 Hz |
0.27 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Comparative Tracking Index | 475 V | 475 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Features | Heat stabilized or stable to heat | |
| ISO Shortname | ISO 1874-PA 66,MHR,14-100,GF30 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- RheTech Products FT4500-01 Thermoplastic Polyolefin, Non-UV Stabilized, Black
- SABIC Innovative Plastics Lexan® FXD1433T PC Copolymer
- Resinoid 2011 Phenolic Molding, Fabric Reinforced
- LG Chemical SEETEC EF320 Ethylene Vinyl Acetate
- Taiwan PU Corporation TPUI-E80 General Grade, Injection Molding Polyester Base TPU
- Westlake EC1924AA Low Density Polyethylene
- Chengdu Polyster 7502 High Performance Grade TPV
- ELASTO UK Dryflex® 422501S SBS Based Material, 50D Hardness, Black
- Dow Corning XIAMETER® PMCPPMX-200 10,000CS Silicone Fluid
- Zeon Chemicals Nipol® 9010 Polyblack Masterbatch
Copyright © lookpolymers.com All Rights Reserved