Solvay Specialty Polymers Ixef® BXT 2000-0203 Polyarylamide (PARA)
| Category | Polymer , Thermoplastic , Polyarylamide (PAA) |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Ixef® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Ixef® BXT 2000-0203 Polyarylamide (PARA).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ixef® BXT 2000-0203 resin was developed specifically for extrusion and blow-molding processes. Unlike grades targeted for injection molding, Ixef® BXT 2000-0203 resin can be successfully extruded into tube, pipe, sheet and film and blow-molded into various profiles. BXT 2000-0203 resin has proven permeation resistance to most automotive fluids and fuels. It also offers low moisture absorption, excellent dimensional stability, and chemical resistance as well as outstanding mechanical properties.Features: Barrier Resin; Fuel Resistant; Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; High Flow; Low Moisture Absorption; Outstanding Surface FinishUses: Blow Molding Applications; Film; Piping; Sheet; TubingAdditional Properties: Melt Flow - (240°C): 6.00 g/10 min; Modulus of Elasticity - ASTM D638 2.48 GPa; Permeation - SAE J2659 (60°C): 0.83 g·mm/m²/atm/24 hr; Tensile Strain at Break - ASTM D638 44 %; Unnotched Izod Impact - ASTM D4812 No BreakInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| Apparent Bulk Density | 0.700 g/cc | 0.0253 lb/in³ | Method B; ASTM D1895 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 39.9 MPa | 5790 psi | ASTM D638 |
| Tensile Strength, Yield | 63.4 MPa | 9200 psi | ASTM D638 |
| 63.8 MPa | 9250 psi | ISO 527-2 | |
| Elongation at Break | 77 % | 77 % | Nominal; ISO 527-2 |
| Elongation at Yield | 3.7 % | 3.7 % | ISO 527-2 |
| 4.0 % | 4.0 % | ASTM D638 | |
| Tensile Modulus | 2.47 GPa | 358 ksi | ISO 527-2 |
| Izod Impact, Notched | 3.50 J/cm | 6.56 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | ISO 180 |
| Izod Impact, Unnotched (ISO) | 190 kJ/m² | 90.4 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 230 °C | 446 °F | DSC |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | Unannealed; ISO 75-2/A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 220 °C | 428 °F | |
| Zone 2 | 235 °C | 455 °F | |
| Zone 3 | 250 °C | 482 °F | |
| Adapter Temperature | 250 °C | 482 °F | |
| Die Cooling Temperature | 250 °C | 482 °F | |
| Roll Temperature | 107 °C | 225 °F | Take-Off Roll |
| Drying Temperature | 85.0 °C @Time 14400 - 28800 sec |
185 °F @Time 4.00 - 8.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Natural | |
| Form | Pellets | |
| Processing Technique | Blow Molding; Extrusion |
Users viewing this material also viewed the following:
- Termopol Termoton® K2GA5050A TPE Compound, based on SEBS and Polyolefins
- Yparex 8125 Polyolefin Adhesive Resin
- 3M Dyneon™ TF 2053 PTFE (discontinued **)
- Mitsubishi Xantar® FC 19 R Polycarbonate
- Latrobe 440â„¢ N-DUR High Quality Martensitic Stainless Steel
- SABIC Innovative Plastics NORYL HN731SE PPE+HIPS (Europe-Africa-Middle East)
- Entec Hypro™ PPH-T30 Homopolymer Polypropylene, 30% Talc Reinforced
- Beijing Evergrow Resources GFF-3 Glass Fiber Felt
- 3M Scotch-Weld™ MG1500 PR Medical Grade Instant Adhesive
- Ineos Nova 5540 High Impact Polystyrene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved