Lanxess Durethan® AKV 25 F30 000000 Nylon 66, 25% Glass Fiber

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled , Nylon 66, Glass Fiber Filled, Flame Retardant
Manufacturer Lanxess
Trade Name Durethan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® AKV 25 F30 000000 Nylon 66, 25% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 66, 25% glass fiber, injection molding, flame retardantInformation provided by LANXESS.
Physical Properties Metric English Comments
Density 1.60 g/cc
0.0578 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 1.2 %
1.2 %
50% RH; ISO 62
Water Absorption at Saturation 3.9 %
3.9 %
ISO 62
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
60x60x2; 290°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
60x60x2; 290°C / MT 80°C; 600 bar; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 100 MPa
14500 psi
conditioned, 5 mm/min; ISO 527-1,-2
150 MPa
21800 psi
5 mm/min; ISO 527-1,-2
Elongation at Break 2.2 %
2.2 %
5 mm/min; ISO 527-1,-2
2.8 %
2.8 %
conditioned, 5 mm/min; ISO 527-1,-2
Tensile Modulus 8.00 GPa
1160 ksi
conditioned, 1 mm/min; ISO 527-1,-2
10.5 GPa
1520 ksi
1 mm/min; ISO 527-1,-2
Flexural Strength 160 MPa
23200 psi
conditioned, 2 mm/min; ISO 178-A
220 MPa
31900 psi
2 mm/min; ISO 178-A
Flexural Modulus 7.30 GPa
1060 ksi
conditioned, 2 mm/min; ISO 178-A
10.0 GPa
1450 ksi
2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) <= 10.0 kJ/m²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1A
10.0 kJ/m²

@Temperature 23.0 °C
 4.76 ft-lb/in²

@Temperature 73.4 °F
 conditioned; ISO 180-1A
Izod Impact, Unnotched (ISO) 40.0 kJ/m²

@Temperature -30.0 °C
 19.0 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1U
40.0 kJ/m²

@Temperature -30.0 °C
 19.0 ft-lb/in²

@Temperature -22.0 °F
 conditioned; ISO 180-1U
45.0 kJ/m²

@Temperature 23.0 °C
 21.4 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1U
45.0 kJ/m²

@Temperature 23.0 °C
 21.4 ft-lb/in²

@Temperature 73.4 °F
 conditioned; ISO 180-1U
Charpy Impact Unnotched 4.00 J/cm²

@Temperature -30.0 °C
 19.0 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eU
4.00 J/cm²

@Temperature -30.0 °C
 19.0 ft-lb/in²

@Temperature -22.0 °F
 conditioned; ISO 179-1eU
5.00 J/cm²

@Temperature 23.0 °C
 23.8 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eU
5.00 J/cm²

@Temperature 23.0 °C
 23.8 ft-lb/in²

@Temperature 73.4 °F
 conditioned; ISO 179-1eU
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 16.7 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1,-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 44.4 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1,-2
Melting Point 260 °C
500 °F
10 °C/min; ISO 11357-1,-3
Deflection Temperature at 0.46 MPa (66 psi) >= 240 °C
>= 464 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 238 °C
460 °F
ISO 75-1,-2
Vicat Softening Point 240 °C
464 °F
50 N; 120 °C/h; ISO 306
Flammability, UL94 V-0

@Thickness 0.400 mm
 V-0

@Thickness 0.0157 in
V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
5VA

@Thickness 1.00 mm
 5VA

@Thickness 0.0394 in
Glow Wire Test 775 °C

@Thickness 0.800 mm
 1430 °F

@Thickness 0.0315 in
 GWIT; IEC 60695-2-13
775 °C

@Thickness 1.50 mm
 1430 °F

@Thickness 0.0591 in
 GWIT; IEC 60695-2-13
875 °C

@Thickness 0.400 mm
 1610 °F

@Thickness 0.0157 in
 GWIT; IEC 60695-2-13
900 °C

@Thickness 3.00 mm
 1650 °F

@Thickness 0.118 in
 GWIT; IEC 60695-2-13
960 °C

@Thickness 0.400 mm
 1760 °F

@Thickness 0.0157 in
 GWFI; IEC 60695-2-12
960 °C

@Thickness 0.800 mm
 1760 °F

@Thickness 0.0315 in
 GWFI; IEC 60695-2-12
960 °C

@Thickness 1.50 mm
 1760 °F

@Thickness 0.0591 in
 GWFI; IEC 60695-2-12
960 °C

@Thickness 3.00 mm
 1760 °F

@Thickness 0.118 in
 GWFI; IEC 60695-2-12
Shrinkage 0.100 %

@Temperature 120 °C,
Time 14400 sec
 0.100 %

@Temperature 248 °F,
Time 4.00 hour
 post-shrinkage, transverse, 60x60x2; ISO 294-4
0.300 %

@Temperature 120 °C,
Time 14400 sec
 0.300 %

@Temperature 248 °F,
Time 4.00 hour
 post-shrinkage, 60x60x2; ISO 294-4
Electrical Properties Metric English Comments
Comparative Tracking Index 400 V
400 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 280 °C
536 °F
Injection molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection molding; ISO 294
Dry Time 2.00 - 6.00 hour

@Temperature 80.0 °C
 2.00 - 6.00 hour

@Temperature 176 °F
Moisture Content 0.030 - 0.12 %
0.030 - 0.12 %
residual; Karl Fischer test