LTL Color Compounds ColorFast® NYA1000 Nylon/ABS Alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend , Nylon |
| Manufacturer | LTL Color Compounds |
| Trade Name | ColorFast® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LTL Color Compounds ColorFast® NYA1000 Nylon/ABS Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon/ABS alloy with high ductility and excellent chemical resistanceAll information provided by LTL Color Compounders, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | 0.125; ASTM D955 |
| Melt Flow | 9.0 g/10 min @Load 3.80 kg, Temperature 260 °C |
9.0 g/10 min @Load 8.38 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 41.4 MPa | 6000 psi | 2.0 in/min; ASTM D638 |
| Elongation at Break | 200 % | 200 % | 2.0 in/min; ASTM D638 |
| Flexural Strength | 59.3 MPa | 8600 psi | 2.0 in/min; ASTM D790 |
| Flexural Modulus | 1.17 GPa | 170 ksi | 2.0 in/min; ASTM D790 |
| Izod Impact, Notched | 6.41 J/cm @Temperature 22.8 °C |
12.0 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | Unannealed (0.250"); ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 204 - 238 °C | 400 - 460 °F | |
| Middle Barrel Temperature | 210 - 232 °C | 410 - 450 °F | |
| Front Barrel Temperature | 221 - 254 °C | 430 - 490 °F | |
| Nozzle Temperature | 216 - 249 °C | 420 - 480 °F | |
| Melt Temperature | 221 - 254 °C | 430 - 490 °F | |
| Mold Temperature | 10.0 - 71.1 °C | 50.0 - 160 °F | |
| Drying Temperature | 85.0 °C | 185 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | nominal; maximum drying time of 8 hours |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | |
| Vent Depth | 0.00254 - 0.00762 cm | 0.00100 - 0.00300 in | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
Users viewing this material also viewed the following:
- RheTech Products G13P100-724UV 13% Glass Fiber Reinforced Polypropylene, UV Stabilized, NH220L Clear Gray
- ExxonMobil Iotek® 7010 Zinc Ionomer Molding/Extrusion Resin (discontinued **)
- Lushan M-20A Adhesive Resin for Multi-layer Oxygen Barrier Pipe
- LyondellBasell Petrothene® LR686001 High Density Polyethylene
- Plenco 6990 Phenolic, Briquette, Injection Molded
- A. Schulman POLYFORT™ FPP 1239H Glass Filled Chemically Coupled Homopolymer Polypropylene
- A. Schulman SCHULAMID® 66 MK20HI 20% Mineral Reinforced, Impact Modified Nylon 66
- Amity Thermosets ATS 131 Phenolic Molding Organic and graphite Filler, Compression Molded
Copyright © lookpolymers.com All Rights Reserved