LG Chemical RS650 ABS

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded
Manufacturer LG Chemical
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical RS650 ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Extrusion Molding, General PurposeApplication: MiscellaneousCAS No. 9003-56-9Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.04 g/cc
1.04 g/cc
ASTM D792
Maximum Moisture Content 0.010
0.010
Extrusion Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0070 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 6.5 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 6.5 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 107
107
ASTM D785
Tensile Strength, Yield 49.0 MPa

@Thickness 3.20 mm
 7110 psi

@Thickness 0.126 in
 50 mm/min; ASTM D638
Elongation at Break 35 %

@Thickness 3.20 mm
 35 %

@Thickness 0.126 in
 50 mm/min; ASTM D638
Elongation at Yield >= 5.0 %

@Thickness 3.20 mm
 >= 5.0 %

@Thickness 0.126 in
 50 mm/min; ASTM D638
Flexural Yield Strength 80.4 MPa

@Thickness 3.20 mm
 11700 psi

@Thickness 0.126 in
 15 mm/min; ASTM D790
Flexural Modulus 2.55 GPa

@Thickness 3.20 mm
 370 ksi

@Thickness 0.126 in
 15 mm/min; ASTM D790
Izod Impact, Notched 2.94 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
 5.51 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
 ASTM D256
3.24 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 6.06 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C

@Thickness 6.40 mm
 203 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 87.0 °C

@Thickness 6.40 mm
 189 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Vicat Softening Point 95.0 °C

@Load 5.00 kg
 203 °F

@Load 11.0 lb
 50°C/h; ASTM D1525
UL RTI, Electrical 60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
Flammability, UL94 HB

@Thickness >=1.50 mm
 HB

@Thickness >=0.0591 in
HB

@Thickness >=3.00 mm
 HB

@Thickness >=0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
Dielectric Strength 37.0 kV/mm
940 kV/in
Arc Resistance 60 - 120 sec
60 - 120 sec
Hot Wire Ignition, HWI 7.0 - 15 sec

@Thickness >=1.50 mm
 7.0 - 15 sec

@Thickness >=0.0591 in
7.0 - 15 sec

@Thickness >=3.00 mm
 7.0 - 15 sec

@Thickness >=0.118 in
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 1.50 mm
 >= 120 arcs

@Thickness 0.0591 in
>= 120 arcs

@Thickness 3.00 mm
 >= 120 arcs

@Thickness 0.118 in
High Voltage Arc-Tracking Rate, HVTR 10.0 - 25.4 mm/min
0.394 - 1.00 in/min
Processing Properties Metric English Comments
Zone 1 180 - 210 °C
356 - 410 °F
Extrusion Molding
Zone 2 190 - 230 °C
374 - 446 °F
Extrusion Molding
Zone 3 200 - 250 °C
392 - 482 °F
Extrusion Molding
Zone 4 200 - 250 °C
392 - 482 °F
Extrusion Molding
Adapter Temperature 200 - 250 °C
392 - 482 °F
Extrusion Molding
Die Temperature 200 - 250 °C
392 - 482 °F
Extrusion Molding
Melt Temperature 200 - 250 °C
392 - 482 °F
Extrusion Molding
Roll Temperature 60.0 - 90.0 °C
140 - 194 °F
Bottom, Extrusion
70.0 - 90.0 °C
158 - 194 °F
Middle, Extrusion
70.0 - 100 °C
158 - 212 °F
Top, Extrusion
Drying Temperature 70.0 - 80.0 °C
158 - 176 °F
Extrusion Molding
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Extrusion Molding