SABIC Innovative Plastics LNP STAT-KON DX03633C PC

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP STAT-KON
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP STAT-KON DX03633C PC.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP STAT-KON* DX03633C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Clean Compounding System, Electrically Conductive.

Physical Properties	Metric	English	Comments
Density	1.27 g/cc	0.0459 lb/inÂ³	ASTM D792
Linear Mold Shrinkage, Flow	0.0038 cm/cm @Time 86400 sec	0.0038 in/in @Time 24.0 hour	ASTM D955
Linear Mold Shrinkage, Transverse	0.0046 cm/cm @Time 86400 sec	0.0046 in/in @Time 24.0 hour	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	87.0 MPa	12600 psi	ASTM D638
Elongation at Break	2.7 %	2.7 %	ASTM D638
Tensile Modulus	6.18 GPa	896 ksi	50 mm/min; ASTM D638
Flexural Strength	143 MPa	20700 psi	ASTM D790
Flexural Modulus	5.57 GPa	808 ksi	ASTM D790
Izod Impact, Notched	0.420 J/cm	0.787 ft-lb/in	ASTM D256
Izod Impact, Unnotched	3.73 J/cm	6.99 ft-lb/in	ASTM D4812

Electrical Properties	Metric	English	Comments
Volume Resistivity	10000 ohm-cm	10000 ohm-cm	ASTM D257