Samsung Cheil Industries Starex® PT-0180 ABS, Unreinforced Painting Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® PT-0180 ABS, Unreinforced Painting Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Water Absorption | 0.30 % @Temperature 23.0 °C |
0.30 % @Temperature 73.4 °F |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Thickness 3.20 mm |
0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 3.7 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.7 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 108 | 108 | ASTM D785 |
| Tensile Strength at Break | 34.3 MPa | 4970 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 39.2 MPa | 5690 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 55 % | 55 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.16 GPa | 313 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 62.8 MPa | 9110 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.16 GPa | 313 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 2.16 J/cm @Thickness 6.35 mm |
4.04 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 2.45 J/cm @Thickness 3.17 mm |
4.59 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C @Thickness 6.40 mm |
203 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C @Thickness 6.40 mm |
187 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 98.0 °C | 208 °F | B/50; ISO R306 |
| 102 °C | 216 °F | B/120; ISO R306 |
Users viewing this material also viewed the following:
- PolyOne Edgetek® NJ-30GF/000 natural Polyamide 12 (Nylon 12)
- Cookson Group Plaskon® SMT-B-1LV Epoxy Molding Compound for PBGAs (discontinued **)
- LTL Color Compounds ColorRxâ„¢ PE3-0202ARX Biocompatible, Antimicrobial LDPE
- SABIC Innovative Plastics LNP Stat-kon AE0039 ABS (Asia Pacific)
- Polyram PlusTek RB845 Nylon 6 for Injection Molding, Impact Modified
- Loctite® 3091 Light Cure Acrylic Adhesive
- Dow Corning SLYGARD® 535 THIXOTROPIC DIELECTRIC GEL
- ATI Allegheny Ludlum AL 453™ Stainless Steel
- A. Schulman ComAlloy Hiloy® 614 Nylon 6, Glass Reinforced
- Seals Eastern 5717 Fluorocarbon-Elastomer
Copyright © lookpolymers.com All Rights Reserved