Arkema Group Orgalloy® LT 5050 Flexible Nylon Alloy (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon, Flexible Alloy
Manufacturer	Arkema
Trade Name	Orgalloy®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group Orgalloy® LT 5050 Flexible Nylon Alloy (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Very flexible polyamide alloy: easy to process, low moisture absorption, good mechanical properties at low temperature. Demonstrate a good balance of properties eg, high flexibility (500 MPa), good thermal performance and ductility at low temperatures.Suited to the extrusion of mandrels and for blow molding of technical parts under the hood (air intake).ISO data provided by the manufacturer, Arkema.

Physical Properties	Metric	English	Comments
Density	1.04 g/cc	0.0376 lb/in³
Melt Flow	2.0 g/10 min @Load 5.00 kg, Temperature 235 °C	2.0 g/10 min @Load 11.0 lb, Temperature 455 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	23.0 MPa	3340 psi	50 mm/min
Elongation at Break	>= 50 %	>= 50 %	Nominal Strain; 50 mm/min
Elongation at Yield	10 %	10 %	50 mm/min
Tensile Modulus	0.460 GPa	66.7 ksi	1 mm/min
Tensile Creep Modulus, 1 hour	420 MPa	60900 psi
Tensile Creep Modulus, 1000 hours	270 MPa	39200 psi

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	10°C/min
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 3.20 mm	HB @Thickness 0.126 in

Electrical Properties	Metric	English
Electrical Resistivity	7.40e+13 ohm-cm	7.40e+13 ohm-cm
Surface Resistance	>= 1.00e+15 ohm	>= 1.00e+15 ohm
Dielectric Constant	3.6 @Frequency 1e+6 Hz	3.6 @Frequency 1e+6 Hz
	3.8 @Frequency 100 Hz	3.8 @Frequency 100 Hz
Dielectric Strength	36.0 kV/mm	914 kV/in
Dissipation Factor	0.050 @Frequency 1e+6 Hz	0.050 @Frequency 1e+6 Hz
	0.11 @Frequency 100 Hz	0.11 @Frequency 100 Hz
Comparative Tracking Index	600 V	600 V