LG Chemical Lupox® GP2306FC PBT+GF30%

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer LG Chemical
Trade Name Lupox®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical Lupox® GP2306FC PBT+GF30%.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Description: Injection Molding, PBT+GF30%, Flame Retardant Application: IT/OA, E&E (Connector)CAS No. 68928-70-1, 65997-17-3, 24968-12-5 and 1309-64-4Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.62 g/cc
1.62 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0030 - 0.010 cm/cm

@Thickness 3.20 mm
 0.0030 - 0.010 in/in

@Thickness 0.126 in
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 127 MPa

@Thickness 3.20 mm
 18400 psi

@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break 3.0 %

@Thickness 3.20 mm
 3.0 %

@Thickness 0.126 in
 5mm/min; ASTM D638
Flexural Yield Strength 186 MPa

@Thickness 3.20 mm
 27000 psi

@Thickness 0.126 in
 1.3mm/min; ASTM D790
Flexural Modulus 8.34 GPa

@Thickness 3.20 mm
 1210 ksi

@Thickness 0.126 in
 1.3mm/min; ASTM D790
Izod Impact, Notched 0.686 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 1.29 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Melting Point 225 °C
437 °F
@ Break; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 215 °C

@Thickness 6.40 mm
 419 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 205 °C

@Thickness 6.40 mm
 401 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 140 °C

@Thickness >=0.710 mm
 284 °F

@Thickness >=0.0280 in
140 °C

@Thickness >=1.50 mm
 284 °F

@Thickness >=0.0591 in
140 °C

@Thickness >=3.00 mm
 284 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 140 °C

@Thickness >=0.710 mm
 284 °F

@Thickness >=0.0280 in
140 °C

@Thickness >=1.50 mm
 284 °F

@Thickness >=0.0591 in
140 °C

@Thickness >=3.00 mm
 284 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 140 °C

@Thickness >=0.710 mm
 284 °F

@Thickness >=0.0280 in
140 °C

@Thickness >=1.50 mm
 284 °F

@Thickness >=0.0591 in
140 °C

@Thickness >=3.00 mm
 284 °F

@Thickness >=0.118 in
Flammability, UL94 V-0

@Thickness >=0.710 mm
 V-0

@Thickness >=0.0280 in
V-0

@Thickness >=1.50 mm
 V-0

@Thickness >=0.0591 in
V-0

@Thickness >=3.00 mm
 V-0

@Thickness >=0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+17 ohm-cm
1.00e+17 ohm-cm
ASTM D257
Dielectric Strength 28.0 kV/mm

@Thickness 1.00 mm
 711 kV/in

@Thickness 0.0394 in
 ASTM D149
Arc Resistance 60 - 120 sec
60 - 120 sec
ASTM D495
Comparative Tracking Index 250 - 400 V
250 - 400 V
Hot Wire Ignition, HWI 7.0 - 15 sec

@Thickness >=0.710 mm
 7.0 - 15 sec

@Thickness >=0.0280 in
30 - 60 sec

@Thickness >=1.50 mm
 30 - 60 sec

@Thickness >=0.0591 in
High Amp Arc Ignition, HAI 60 - 120 arcs

@Thickness 0.710 mm
 60 - 120 arcs

@Thickness 0.0280 in
60 - 120 arcs

@Thickness 1.50 mm
 60 - 120 arcs

@Thickness 0.0591 in
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
Processing Properties Metric English Comments
Rear Barrel Temperature 235 - 250 °C
455 - 482 °F
Injection Molding
Middle Barrel Temperature 240 - 250 °C
464 - 482 °F
Injection Molding
Front Barrel Temperature 245 - 255 °C
473 - 491 °F
Injection Molding
Nozzle Temperature 245 - 255 °C
473 - 491 °F
Injection Molding
Melt Temperature 245 - 255 °C
473 - 491 °F
Injection Molding
Mold Temperature 60.0 - 100 °C
140 - 212 °F
Injection Molding
Drying Temperature 120 °C
248 °F
Injection Molding
Dry Time 4.00 - 5.00 hour
4.00 - 5.00 hour
Injection Molding