LG Chemical LUSEP GP2400 PPS+GF40%, General Purpose

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 40% Glass Fiber Filler
Manufacturer LG Chemical
Trade Name LUSEP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUSEP GP2400 PPS+GF40%, General Purpose.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Injection Molding, PPS+GF40%, General PurposeApplication: Pump Units, Motor Units, etc.CAS No. 25212-74-2 and 65997-17-3Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.65 g/cc
1.65 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0010 - 0.0020 cm/cm

@Thickness 3.20 mm
 0.0010 - 0.0020 in/in

@Thickness 0.126 in
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 152 MPa

@Thickness 3.20 mm
 22000 psi

@Thickness 0.126 in
 5mm/min; ASTM D638
Elongation at Break 1.0 - 2.0 %

@Thickness 3.20 mm
 1.0 - 2.0 %

@Thickness 0.126 in
 5mm/min; ASTM D638
Flexural Yield Strength 226 MPa

@Thickness 3.20 mm
 32700 psi

@Thickness 0.126 in
 1.3mm/min; ASTM D790
Flexural Modulus 11.8 GPa

@Thickness 3.20 mm
 1710 ksi

@Thickness 0.126 in
 1.3mm/min; ASTM D790
Izod Impact, Notched 0.686 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 1.29 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) >= 250 °C

@Thickness 6.40 mm
 >= 482 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) >= 250 °C

@Thickness 6.40 mm
 >= 482 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 130 °C

@Thickness >=0.320 mm
 266 °F

@Thickness >=0.0126 in
130 °C

@Thickness >=0.750 mm
 266 °F

@Thickness >=0.0295 in
130 °C

@Thickness >=1.70 mm
 266 °F

@Thickness >=0.0669 in
130 °C

@Thickness >=3.00 mm
 266 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 130 °C

@Thickness >=0.320 mm
 266 °F

@Thickness >=0.0126 in
130 °C

@Thickness >=0.750 mm
 266 °F

@Thickness >=0.0295 in
130 °C

@Thickness >=1.70 mm
 266 °F

@Thickness >=0.0669 in
130 °C

@Thickness >=3.00 mm
 266 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 130 °C

@Thickness >=0.320 mm
 266 °F

@Thickness >=0.0126 in
130 °C

@Thickness >=0.750 mm
 266 °F

@Thickness >=0.0295 in
130 °C

@Thickness >=1.70 mm
 266 °F

@Thickness >=0.0669 in
130 °C

@Thickness >=3.00 mm
 266 °F

@Thickness >=0.118 in
Flammability, UL94 V-0

@Thickness >=0.320 mm
 V-0

@Thickness >=0.0126 in
V-0

@Thickness >=0.750 mm
 V-0

@Thickness >=0.0295 in
V-0

@Thickness >=1.70 mm
 V-0

@Thickness >=0.0669 in
V-0

@Thickness >=3.00 mm
 V-0

@Thickness >=0.118 in
5VA

@Thickness >=1.70 mm
 5VA

@Thickness >=0.0669 in
Electrical Properties Metric English Comments
Dielectric Strength 16.0 kV/mm
406 kV/in
Hot Wire Ignition, HWI 7.0 - 15 sec

@Thickness >=0.750 mm
 7.0 - 15 sec

@Thickness >=0.0295 in
15 - 30 sec

@Thickness >=1.70 mm
 15 - 30 sec

@Thickness >=0.0669 in
60 - 120 sec

@Thickness >=3.00 mm
 60 - 120 sec

@Thickness >=0.118 in
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.750 mm
 >= 120 arcs

@Thickness 0.0295 in
>= 120 arcs

@Thickness 1.70 mm
 >= 120 arcs

@Thickness 0.0669 in
>= 120 arcs

@Thickness 3.00 mm
 >= 120 arcs

@Thickness 0.118 in
Processing Properties Metric English Comments
Rear Barrel Temperature 300 °C
572 °F
Injection Molding
Middle Barrel Temperature 310 °C
590 °F
Injection Molding
Front Barrel Temperature 320 °C
608 °F
Injection Molding
Nozzle Temperature 330 °C
626 °F
Injection Molding
Melt Temperature 300 - 330 °C
572 - 626 °F
Injection Molding
Mold Temperature 120 - 150 °C
248 - 302 °F
Injection Molding
Drying Temperature 100 - 120 °C
212 - 248 °F
Injection Molding
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Injection Molding
Screw Speed >= 100 rpm
>= 100 rpm
Injection Molding