SABIC Innovative Plastics LNP THERMOCOMP DF0049P PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DF0049P PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* DF0049P is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Exceptional Processing, Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ASTM D792 |
| 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 108 MPa | 15700 psi | ASTM D638 |
| 108 MPa | 15700 psi | ISO 527 | |
| Elongation at Break | 2.7 % | 2.7 % | ISO 527 |
| 3.0 % | 3.0 % | ASTM D638 | |
| Tensile Modulus | 6.85 GPa | 994 ksi | 50 mm/min; ASTM D638 |
| 6.95 GPa | 1010 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 165 MPa | 23900 psi | ASTM D790 |
| 165 MPa | 23900 psi | ISO 178 | |
| Flexural Modulus | 6.08 GPa | 882 ksi | ASTM D790 |
| 6.21 GPa | 901 ksi | ISO 178 | |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.79 J/cm | 5.23 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 47.0 kJ/m² | 22.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 11.0 J | 8.11 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 9.00 J | 6.64 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 23.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 23.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 75.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
42.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 75.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
42.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 135 °C @Thickness 3.20 mm |
275 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 0.850 mm |
V-0 @Thickness 0.0335 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- Resinlab® CYNERGY CA6702 Adhesive
- Plenco 307 Black Impact Grade Mineral/Flock Filled Phenolic Molding Compound (discontinued **)
- Kolon KOPA® KN332G30VO G/F Reinforced & Flame Retardant Nylon 66
- SABIC Innovative Plastics LNP LUBRICOMP RFL16 PA 66
- Formosa Plastics Formolene® 2315N Impact Copolymer Polypropylene
- DuPont Performance Polymers Minlon® 11C140 BK086 Nylon 66 (Unverified Data**)
- DuPont Performance Polymers VESPEL TP-8212 Polyimide
- Ashley Polymers Ashlene® R3144 PC/PBT
- 3M Novec™ 1702 Electronic Grade Coating
- Resinlab® RC8020 Anaerobic Retaining Compound
Copyright © lookpolymers.com All Rights Reserved