Shell Carilon® D26FX100 Polyketone, General-Purpose Extrusion Grade  (discontinued **)

Category Polymer , Thermoplastic , Polyketone
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Shell Carilon® D26FX100 Polyketone, General-Purpose Extrusion Grade  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON Polymer D26FX100 is a general-purpose extrusion grade with mechanical properties that classify it as an engineering thermoplastic. This grade exhibits high chemical resistance and barrier performance. Moreover, this grade shows a high impact resistance, both at room temperature and at lower temperatures, and good creep performance. CARILON Polymer D26FX100 can also withstand short-term exposure to elevated temperatures. CARILON Polymer D26FX100 is processable on standard extrusion equipment and may be considered for the production of tubes, industrial hoses, monofilaments, coatings for cable and wire. It is also possible to coextrude CARILON Polymer D26FX100 with other materials, typically to be employed as a barrier layer in containment applications.Data provided by Shell Chemical.
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
ASTM D792
Water Absorption 0.021 %
0.021 %
At Saturation; ASTM D570
Water Absorption at Saturation 2.1 %
2.1 %
at saturation; ASTM D570
Melt Flow 6.0 g/10 min

@Load 2.16 kg,
Temperature 240 °C
6.0 g/10 min

@Load 4.76 lb,
Temperature 464 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 105
105
ASTM D785
Hardness, Shore D 75
75
ISO 868
Tensile Strength, Ultimate 55.0 MPa
7980 psi
ASTM D638
Tensile Strength, Yield 60.0 MPa
8700 psi
ASTM D638
Elongation at Break >= 300 %
>= 300 %
ASTM D638
Elongation at Yield 25 %
25 %
ASTM D638
Tensile Modulus 1.60 GPa
232 ksi
ASTM D638
Flexural Strength 55.0 MPa
7980 psi
at 5% strain; ASTM D790
Flexural Modulus 1.60 GPa
232 ksi
ASTM D790
Izod Impact, Notched 2.40 J/cm
4.50 ft-lb/in
0.500 J/cm

@Temperature -40.0 °C
0.937 ft-lb/in

@Temperature -40.0 °F
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D256
Charpy Impact Unnotched NB
NB
ISO 179
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched 1.80 J/cm²
8.57 ft-lb/in²
ISO 179
0.400 J/cm²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Taber Abrasion, mg/1000 Cycles 12
12
1 kg load; CS-17 Wheel; ASTM D1044
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
Maximum Service Temperature, Air 90.0 °C
194 °F
UL-746B Long Term Relative temperature Index; Mechanical w/o Impact
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 105 °C
221 °F
ASTM D648
Vicat Softening Point 210 °C
410 °F
ASTM D1525
UL RTI, Mechanical with Impact 85.0 °C

@Thickness 0.750 mm
185 °F

@Thickness 0.0295 in
UL-746B
UL RTI, Mechanical without Impact 90.0 °C

@Thickness 0.750 mm
194 °F

@Thickness 0.0295 in
UL-746B
Flammability, UL94 HB
HB
Oxygen Index 21 %
21 %
ISO 4589
Electrical Properties Metric English Comments
Arc Resistance 60 - 120 sec
60 - 120 sec
UL-746A rating 6 (60-120 sec)
Comparative Tracking Index >= 600 V
>= 600 V
UL746A
Processing Properties Metric English Comments
Processing Temperature 240 °C
464 °F
At Die