LG Chemical LUPOY GP5106F PC/ABS+GF10%, Flame Retardance

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC)
Manufacturer LG Chemical
Trade Name LUPOY
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF LG Chemical LUPOY GP5106F PC/ABS+GF10%, Flame Retardance.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Description: Injection Molding, PC/ABS+GF10%, Flame RetardanceApplication: IT/OA (Housing)CAS: 103598-77-2, 9003-56-9, 68928-70-1, 1309-64-4 and 65997-17-3Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.25 g/cc
1.25 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm
<br>@Thickness 3.20 mm
 0.0020 - 0.0040 in/in
<br>@Thickness 0.126 in
 ASTM D955
Melt Flow 4.0 g/10 min
<br>@Load 2.16 kg,<br> Temperature 250 °C
 4.0 g/10 min
<br>@Load 4.76 lb,<br> Temperature 482 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 115
115
ASTM D785
Tensile Strength, Yield 65.7 MPa
<br>@Thickness 3.20 mm
 9530 psi
<br>@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break 7.0 %
<br>@Thickness 3.20 mm
 7.0 %
<br>@Thickness 0.126 in
 50mm/min; ASTM D638
Flexural Yield Strength 108 MPa
<br>@Thickness 3.20 mm
 15600 psi
<br>@Thickness 0.126 in
 10mm/min; ASTM D790
Flexural Modulus 3.92 GPa
<br>@Thickness 3.20 mm
 569 ksi
<br>@Thickness 0.126 in
 10mm/min; ASTM D790
Izod Impact, Notched 0.686 J/cm
<br>@Thickness 3.20 mm,<br> Temperature 23.0 °C
 1.29 ft-lb/in
<br>@Thickness 0.126 in,<br> Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 113 °C
<br>@Thickness 6.40 mm
 235 °F
<br>@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 60.0 °C
<br>@Thickness >=1.70 mm
 140 °F
<br>@Thickness >=0.0669 in
UL RTI, Mechanical with Impact 60.0 °C
<br>@Thickness >=1.70 mm
 140 °F
<br>@Thickness >=0.0669 in
UL RTI, Mechanical without Impact 60.0 °C
<br>@Thickness >=1.70 mm
 140 °F
<br>@Thickness >=0.0669 in
Flammability, UL94 V-0
<br>@Thickness >=1.70 mm
 V-0
<br>@Thickness >=0.0669 in
Processing Properties Metric English Comments
Rear Barrel Temperature 220 - 240 °C
428 - 464 °F
Injection Molding
Middle Barrel Temperature 235 - 255 °C
455 - 491 °F
Injection Molding
Front Barrel Temperature 250 - 265 °C
482 - 509 °F
Injection Molding
Nozzle Temperature 250 - 265 °C
482 - 509 °F
Injection Molding
Melt Temperature 235 - 265 °C
455 - 509 °F
Injection Molding
Mold Temperature 50.0 - 80.0 °C
122 - 176 °F
Injection Molding
Drying Temperature 75.0 - 85.0 °C
167 - 185 °F
Injection Molding
Dry Time 3.00 - 5.00 hour
3.00 - 5.00 hour
Injection Molding
Back Pressure 0.00200 - 0.00600 MPa
0.290 - 0.870 psi
Injection Molding
Screw Speed 40 - 70 rpm
40 - 70 rpm
Injection Molding