SABIC Innovative Plastics NORYL HNA033 PPE+HIPS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL HNA033 PPE+HIPS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl* HNA033 resin is an unfilled modified polyphenylene ether resin designed to withstand several cycles in an autoclave. This resin is suitable for multiple conversion routes and is available in custom colors. Noryl HNA033 resin may be an excellent material candidate for applications requiring multiple sterilization cycles. Noryl HNA033 resin is biocompatible per ISO 10993 (color dependent).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Density | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.15 % | 0.15 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm @Thickness 3.20 mm |
0.0070 - 0.0090 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 8.3 g/10 min @Load 5.00 kg, Temperature 300 °C |
8.3 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Melt Index of Compound | 8.0 g/10 min @Load 5.00 kg, Temperature 300 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 |
| 57.0 MPa | 8270 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 68.0 MPa | 9860 psi | 50 mm/min; ISO 527 |
| 71.0 MPa | 10300 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 14.8 % | 14.8 % | 50 mm/min; ISO 527 |
| 30 % | 30 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 5.2 % | 5.2 % | 50 mm/min; ISO 527 |
| 5.3 % | 5.3 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.31 GPa | 335 ksi | 5 mm/min; ASTM D638 |
| 2.60 GPa | 377 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 100 MPa | 14500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 107 MPa | 15500 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 2.46 GPa | 357 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.59 GPa | 376 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.92 J/cm | 3.60 ft-lb/in | ASTM D256 |
| 1.44 J/cm @Temperature -30.0 °C |
2.70 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | 80*10*4; ISO 180/1A |
| 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 47.0 J @Temperature 23.0 °C |
34.7 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
39.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 70.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
39.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 68.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 68.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 160 °C | 320 °F | Rate B/50; ISO 306 |
| 161 °C | 322 °F | Rate B/50; ASTM D1525 | |
| 162 °C | 324 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPH GF10030 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled
- Polykemi AB POLYfill PPH GF8020 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled
- Dow Pellethane® 2102-85A Polyurethane Elastomer, Polyester Polycaprolactone Based (discontinued **)
- Hexion Bakelite™ X22 Phenolic Formaldehyde Resin, UL Listed (discontinued **)
- Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 1.0 mm thick sheet
- Mitsubishi Hostaphan® WN, 250 micron Nominal Thickness Translucent White Polyethylene Terephthalate Film
- Solvay TECHNYL® A 218W V15 PA66, 15% glass fiber, DRY
- Fainplast Compounds PH 90/AS Flexible PVC, Transparent Extrusion
- 3M Scotch® 829 Packing List Pouch Tape
- Colorite Polymers 4875 General Purpose Vinyl Compound
Copyright © lookpolymers.com All Rights Reserved