- Cossa Polimeri ESTAPROP H 0560 GFCTG Polypropylene, 30% Mixed Filler
Cossa Polimeri ESTAPROP H 0560 GFCTG Polypropylene, 30% Mixed Filler
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Glass/Mineral Reinforced |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTAPROP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTAPROP H 0560 GFCTG Polypropylene, 30% Mixed Filler.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PP homopolymer 30% mixed fillerGood physical and mechanical characteristicsInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | ASTM D 955 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ASTM D 638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D 638 |
| Tensile Modulus | 4.70 GPa | 682 ksi | ASTM D 638 |
| Flexural Modulus | 4.30 GPa | 624 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.350 J/cm @Temperature -20.0 °C |
0.656 ft-lb/in @Temperature -4.00 °F |
ASTM D 638 |
| 0.500 J/cm @Temperature 0.000 °C |
0.937 ft-lb/in @Temperature 32.0 °F |
ASTM D 638 | |
| 0.700 J/cm @Temperature 23.0 °C |
1.31 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | 120°C/hr; ASTM D 648 |
| Vicat Softening Point | 105 °C @Load 5.00 kg |
221 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Rigid Extrusion 87160 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Murtfeldt Material ”S”® 1000 Green Polyethylene
- Arlon Thermabond® R37340X008 Primerless Electronic Adhesive (discontinued **)
- Nilit FRIANYL B63 FK 1020 Nylon 6 for injection molding, 10% glass fiber and 20% glass ball reinforced
- Solvay Specialty Polymers Udel® P-1750 MR Polysulfone (PSU) (Unverified Data**)
- Sax Polymers SAXAMID 236F4Q32 Nylon 6.6, 20% Glass Fiber
- Daikin DAI-EL G-751 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content
- ATI Allvac® Vasco® 4340 Specialty Steel, Heat Treatment: 899°C (1650°F) Q+T
Copyright © lookpolymers.com All Rights Reserved