BLUESTAR LXS 115 PPE-PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) , Polystyrene + Polyphenylene Ether, Unreinforced |
| Manufacturer | BLUESTAR |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BLUESTAR LXS 115 PPE-PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Typical Applications: Auto connect partsFire RatedInformation provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Water Absorption | 0.10 % @Temperature 23.0 °C, Time 86400 sec |
0.10 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 15 g/10 min @Load 5.00 kg, Temperature 300 °C |
15 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa | 9430 psi | type I; ASTM D638 |
| Elongation at Break | 28 % | 28 % | type I; ASTM D638 |
| Flexural Strength | 92.0 MPa | 13300 psi | 2.6 mm/min; ASTM D790 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2.6 mm/min; ASTM D790 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C @Thickness 6.40 mm |
302 °F @Thickness 0.252 in |
ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
|
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
||
| V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
Users viewing this material also viewed the following:
- Nilit RECONYL A SG30 Recycled nylon 6.6 for injection molding, 30% mineral filled
- Fiberfil® J-60/10/CC/30/E NATL Polypropylene Homopolymer, 10% FiberGlass and 30% Calcium Carbonate Reinforced, Chemically coupled
- Lehmann & Voss LUVOCOM® 1104-7824 Polyether ketone, with carbon fiber, easy flowing
- Teknor Apex APEX® 3311-55 Polyvinyl Chloride, Flexible
- Silberline Sparkle Silvex® Premier 838-20-C
- AK Steel ASTM A 1011, Class 2 Formable, Grade 55F Hot Rolled Carbon Steel, Medium/High Strength Low Alloy Steel (HSLA-F)
- Ashley Polymers Ashlene® 525-13G Nylon 66, 13% Glass Reinforced
- Axiall 6570 Moldings & Extrusions Flexible PVC
- Azoty Tarnow™ TARNOFORM 300 HI6 POM
- Plastcom SLOVALEN PC 92 T 40 PP, 40% mineral filling
Copyright © lookpolymers.com All Rights Reserved