LG Chemical LUPOY ER5001RF PC/ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOY ER5001RF PC/ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PC/ABS, Halogen Free Flame Retardant, EPEATApplication: IT&OA (All in One PC & Notebook PC housing)CAS: 103598-77-2, 9003-56-9 and 181028-79-5Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 18 g/10 min @Load 2.16 kg, Temperature 250 °C |
18 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 58.8 MPa @Thickness 3.20 mm |
8530 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 93.2 MPa @Thickness 3.20 mm |
13500 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 2.55 GPa @Thickness 3.20 mm |
370 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | >= 4.90 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
>= 9.18 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C @Thickness 6.40 mm |
198 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 60.0 °C | 140 °F | |
| UL RTI, Mechanical with Impact | 60.0 °C | 140 °F | |
| UL RTI, Mechanical without Impact | 60.0 °C | 140 °F | |
| Flammability, UL94 | V-0 @Thickness >=1.20 mm |
V-0 @Thickness >=0.0472 in |
|
| V-0 @Thickness >=1.50 mm |
V-0 @Thickness >=0.0591 in |
||
| V-0 @Thickness >=3.00 mm |
V-0 @Thickness >=0.118 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 225 - 240 °C | 437 - 464 °F | Injection Molding |
| Middle Barrel Temperature | 240 - 255 °C | 464 - 491 °F | Injection Molding |
| Front Barrel Temperature | 250 - 265 °C | 482 - 509 °F | Injection Molding |
| Nozzle Temperature | 250 - 265 °C | 482 - 509 °F | Injection Molding |
| Melt Temperature | 235 - 265 °C | 455 - 509 °F | Injection Molding |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | Injection Molding |
| Drying Temperature | 75.0 - 85.0 °C | 167 - 185 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| Back Pressure | 0.0200 - 0.0600 MPa | 2.90 - 8.70 psi | Injection Molding |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Polymer Resources NY6-IM1 Nylon 6, Impact Modified
- Solvay Specialty Polymers Hylar® MP10 PVDF Polyvinylidene Fluoride (discontinued **)
- Gwent Electronic Materials C2070920D1 Depolymerisable Carbon Ink
- Lushan EV1050G1 EVA Film for Encapsulating Solar modules, Ultra Fast Cure
- Multibase C6-515 Dow-Corning Class VI Elastomer
- Plenco 7487 Phenolic, Granular, Transfer Molded
- Zircar Zirconia ZYW-15 Zirconia Cloth Insulation
- Lubrizol ESTANE® 58142 Ester Based Thermoplastic Polyurethane (European Grade)
- ChevronTexaco Syntholube® ISO 100 Compressor Oil
- Polyplastics Duracon® M25-45 Acetal Co-polymer (POM), Weather resistance, High viscosity
Copyright © lookpolymers.com All Rights Reserved