LG Chemical LUMID HI2152A(W) PA6+GF15%, High Impact
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled , Nylon 6, Impact Grade |
| Manufacturer | LG Chemical |
| Trade Name | LUMID |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUMID HI2152A(W) PA6+GF15%, High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, PA6+GF15%, High ImpactApplication: Automotive PartsCAS No. 25038-54-4, 9010-79-1 and 65997-17-3Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Water Absorption | 1.2 % | 1.2 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.010 cm/cm @Thickness 3.20 mm |
0.0050 - 0.010 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Yield | 96.1 MPa @Thickness 3.20 mm |
13900 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Elongation at Break | 4.5 % @Thickness 3.20 mm |
4.5 % @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Flexural Yield Strength | 137 MPa @Thickness 3.20 mm |
19900 psi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| Flexural Modulus | 4.31 GPa @Thickness 3.20 mm |
626 ksi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 0.588 J/cm @Thickness 6.40 mm, Temperature -30.0 °C |
1.10 ft-lb/in @Thickness 0.252 in, Temperature -22.0 °F |
ASTM D256 |
| 1.77 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
3.31 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 36.0 µm/m-°C | 20.0 µin/in-°F | ASTM D696 |
| Melting Point | 220 °C | 428 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C @Thickness 6.40 mm |
392 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 21.0 kV/mm @Thickness 1.00 mm |
533 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Arc Resistance | 180 sec | 180 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 280 °C | 500 - 536 °F | Injection Molding |
| Middle Barrel Temperature | 250 - 270 °C | 482 - 518 °F | Injection Molding |
| Front Barrel Temperature | 260 - 285 °C | 500 - 545 °F | Injection Molding |
| Nozzle Temperature | 260 - 290 °C | 500 - 554 °F | Injection Molding |
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | Injection Molding |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
Users viewing this material also viewed the following:
- Palm Labs Adhesives Turbo Fuse Series 115SI Surface Insensitive (20 Viscosity) Rapid Bonding Adhesive
- NOVA Chemicals Sclair® 58D HDPE Blow Molding Resin (discontinued **)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 60 PHR N220 Filler
- Eurotec® Tecomid® NB30 GR13 BK EF PA6, 13% glass fiber reinforced, black, suitable for electrostatic powder coating
- 3M 7041 Screen Printable Polyester Performance Label Products
- Arlon Ultrapad™ D 65 (55073R062) 0.0622 (1.58 mm) Cured Silicone Rubber with Fiberglass Substrate
- BASF Triisopropanolamine
- ExxonMobil Geolast® 703-45 Thermoplastic Elastomer
- BASF Styrodur® 3035 CN Extruded Rigid Polystyrene Foam (Europe)
Copyright © lookpolymers.com All Rights Reserved