Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
Trade Name | INCONEL® |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Special Metals INCONEL® alloy 693.pdf |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 7.77 g/cc | 0.281 lb/in³ |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 882.6 MPa | 128000 psi | Hot-rolled and annealed plate |
937.7 MPa | 136000 psi | Cold-drawn and annealed tubing | |
Tensile Strength, Yield | 489.5 MPa @Strain 0.200 % |
71000 psi @Strain 0.200 % |
Hot-rolled and annealed plate |
530.9 MPa @Strain 0.200 % |
77000 psi @Strain 0.200 % |
Cold-drawn and annealed tubing | |
Elongation at Break | 42 % | 42 % | Cold-drawn and annealed tubing |
45 % | 45 % | Hot-rolled and annealed plate | |
Rupture Strength | 22.1 MPa @Temperature 871 °C, Time 3.60e+7 sec |
3200 psi @Temperature 1600 °F, Time 10000 hour |
|
38.6 MPa @Temperature 871 °C, Time 3.60e+6 sec |
5600 psi @Temperature 1600 °F, Time 1000 hour |
||
68.9 MPa @Temperature 871 °C, Time 360000 sec |
10000 psi @Temperature 1600 °F, Time 100 hour |
||
159 MPa @Temperature 649 °C, Time 3.60e+7 sec |
23000 psi @Temperature 1200 °F, Time 10000 hour |
||
228 MPa @Temperature 649 °C, Time 3.60e+6 sec |
33000 psi @Temperature 1200 °F, Time 1000 hour |
||
310 MPa @Temperature 649 °C, Time 360000 sec |
45000 psi @Temperature 1200 °F, Time 100 hour |
||
Modulus of Elasticity | 137 GPa @Temperature 800 °C |
19900 ksi @Temperature 1470 °F |
|
165 GPa @Temperature 500 °C |
23900 ksi @Temperature 932 °F |
||
194 GPa @Temperature 100 °C |
28100 ksi @Temperature 212 °F |
||
196 GPa @Temperature 21.0 °C |
28400 ksi @Temperature 69.8 °F |
||
Charpy Impact, Notched | 26.3 J/cm² @Temperature 704 °C, Time 3.60e+6 sec |
125 ft-lb/in² @Temperature 1300 °F, Time 1000 hour |
|
27.5 J/cm² @Temperature 649 °C, Time 3.60e+6 sec |
131 ft-lb/in² @Temperature 1200 °F, Time 1000 hour |
||
39.0 J/cm² @Temperature 760 °C, Time 3.60e+6 sec |
186 ft-lb/in² @Temperature 1400 °F, Time 1000 hour |
||
68.6 J/cm² @Temperature 593 °C, Time 3.60e+6 sec |
326 ft-lb/in² @Temperature 1100 °F, Time 1000 hour |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 13.04 µm/m-°C @Temperature 100 °C |
7.244 µin/in-°F @Temperature 212 °F |
|
14.8 µm/m-°C @Temperature 500 °C |
8.22 µin/in-°F @Temperature 932 °F |
||
17.01 µm/m-°C @Temperature 900 °C |
9.450 µin/in-°F @Temperature 1650 °F |
||
Specific Heat Capacity | 0.455 J/g-°C @Temperature 23.0 °C |
0.109 BTU/lb-°F @Temperature 73.4 °F |
|
0.484 J/g-°C @Temperature 100 °C |
0.116 BTU/lb-°F @Temperature 212 °F |
||
0.560 J/g-°C @Temperature 500 °C |
0.134 BTU/lb-°F @Temperature 932 °F |
||
0.642 J/g-°C @Temperature 900 °C |
0.153 BTU/lb-°F @Temperature 1650 °F |
||
Thermal Conductivity | 9.10 W/m-K @Temperature 23.0 °C |
63.2 BTU-in/hr-ft²-°F @Temperature 73.4 °F |
|
10.7 W/m-K @Temperature 100 °C |
74.3 BTU-in/hr-ft²-°F @Temperature 212 °F |
||
17.8 W/m-K @Temperature 500 °C |
124 BTU-in/hr-ft²-°F @Temperature 932 °F |
||
23.6 W/m-K @Temperature 900 °C |
164 BTU-in/hr-ft²-°F @Temperature 1650 °F |
||
Melting Point | 1317 - 1367 °C | 2403 - 2493 °F | |
Solidus | 1317 °C | 2403 °F | |
Liquidus | 1367 °C | 2493 °F |
Component Elements Properties | Metric | English | Comments |
---|---|---|---|
Aluminum, Al | 2.5 - 4.0 % | 2.5 - 4.0 % | |
Carbon, C | <= 0.15 % | <= 0.15 % | |
Chromium, Cr | 27 - 31 % | 27 - 31 % | |
Copper, Cu | <= 0.50 % | <= 0.50 % | |
Iron, Fe | 2.5 - 6.0 % | 2.5 - 6.0 % | |
Manganese, Mn | <= 1.0 % | <= 1.0 % | |
Nickel, Ni | 53.34 - 67.5 % | 53.34 - 67.5 % | as remainder |
Niobium, Nb (Columbium, Cb) | 0.50 - 2.5 % | 0.50 - 2.5 % | |
Silicon, Si | <= 0.50 % | <= 0.50 % | |
Sulfur, S | <= 0.010 % | <= 0.010 % | |
Titanium, Ti | <= 1.0 % | <= 1.0 % |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Electrical Resistivity | 0.0001168 ohm-cm | 0.0001168 ohm-cm |