LG Chemical LUMID HI1202A(W) PA6, High Impact
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade |
| Manufacturer | LG Chemical |
| Trade Name | LUMID |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUMID HI1202A(W) PA6, High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, PA6, High ImpactApplication: Electric/Electronic PartsCAS No. 25038-54-4 and 9010-79-1Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Water Absorption | 1.1 % | 1.1 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.014 - 0.018 cm/cm @Thickness 3.20 mm |
0.014 - 0.018 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Yield | 51.0 MPa @Thickness 3.20 mm |
7400 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 60 % @Thickness 3.20 mm |
60 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 68.6 MPa @Thickness 3.20 mm |
9960 psi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| Flexural Modulus | 1.77 GPa @Thickness 3.20 mm |
256 ksi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 8.34 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
15.6 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ASTM D696 |
| Melting Point | 220 °C | 428 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C @Thickness 6.40 mm |
266 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C @Thickness 6.40 mm |
122 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.8 @Frequency 1.00e+6 Hz |
2.8 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 20.0 kV/mm @Thickness 1.00 mm |
508 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Arc Resistance | 195 sec | 195 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 230 - 260 °C | 446 - 500 °F | Injection Molding |
| Middle Barrel Temperature | 240 - 270 °C | 464 - 518 °F | Injection Molding |
| Front Barrel Temperature | 250 - 280 °C | 482 - 536 °F | Injection Molding |
| Nozzle Temperature | 250 - 280 °C | 482 - 536 °F | Injection Molding |
| Melt Temperature | 250 - 280 °C | 482 - 536 °F | Injection Molding |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
Users viewing this material also viewed the following:
- Mytex Polymers AN16L(W)-D56 Polypropylene, Talc filled, Compounded, Elastomer, Impact modified
- DSM Akulon® K224-HGR24 Nylon 6-30% Glass Fiber and Glass Bead Reinforced (European Grade) (Dry) (discontinued
- Overview of materials for Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler
- Less Common Metals Sm2Co17 Samarium Cobalt Alloy; Vacuum Induction Melting & Casting
- Lord Adhesives HPC-5B Hydrogenated Nitrile Butadiene Rubber Coating
- Gwent Electronic Materials C2011004P5 Platinum Ink
- Lehmann & Voss LUVOCOM® 1800-7432 PET, with PTFE
- SABIC Innovative Plastics ULTEM 9076 PEI
- Cossa Polimeri ESTAPROP H 1660 GFC Polypropylene, 30% Glass Filled
- Arkema Group Pebax® MP 1878 SA 01 Polyether Block Amide (PEBA)
Copyright © lookpolymers.com All Rights Reserved