Manifattura Cattaneo PET Polyethylene Terephthalate
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Unreinforced |
| Manufacturer | Manifattura Cattaneo spa |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Manifattura Cattaneo PET Polyethylene Terephthalate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.25 % @Temperature 23.0 °C |
0.25 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | 0.50 % | 0.50 % | ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 96 | 96 | ISO 2039-2 |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | ISO 527 |
| Elongation at Break | 15 % | 15 % | ISO 527 |
| Tensile Modulus | 3.70 GPa | 537 ksi | ISO 527 |
| Compressive Yield Strength | 26.0 MPa @Strain 1.00 % |
3770 psi @Strain 1.00 % |
ISO 604 |
| Poissons Ratio | 0.44 | 0.44 | |
| Charpy Impact Unnotched | >= 5.00 J/cm² | >= 23.8 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | ISO 179 |
| Coefficient of Friction, Dynamic | 0.25 | 0.25 | on polished steel; MPC Test |
| Coefficient of Friction, Static | 0.19 | 0.19 | on polished steel; MPC Test |
| K Factor (Wear Factor) | 0.60 | 0.60 | µm/s. PV = 0.1 MPa-m/s; max P = 25 MPa; MPC Test |
| Limiting Pressure Velocity | 0.0800 MPa-m/sec | 2280 psi-ft/min | without lubrication; MPC Test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C @Temperature 23.0 - 100 °C |
44.4 µin/in-°F @Temperature 73.4 - 212 °F |
ASTM D696 |
| Thermal Conductivity | 0.290 W/m-K | 2.01 BTU-in/hr-ft²-°F | DOM 52612 |
| Maximum Service Temperature, Air | 115 °C | 239 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75 |
| Minimum Service Temperature, Air | -20.0 °C | -4.00 °F | |
| Flammability, UL94 | HB | HB | |
| V-2 | V-2 | ||
| Oxygen Index | 25 % | 25 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+17 ohm-cm | >= 1.00e+17 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | IEC 60094 |
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz |
3.2 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 22.0 kV/mm @Thickness 2.00 mm |
559 kV/in @Thickness 0.0787 in |
IEC 60243 |
| Dielectric Loss Index | 0.014 @Frequency 1.00e+6 Hz |
0.014 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Compliance Properties | Metric | English | Comments |
|---|---|---|---|
| FDA | Yes | Yes |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | White | |
| UV Resistance | N |
Users viewing this material also viewed the following:
- MV Labs HG800 HgO Mercury(II) oxide
- PolyOne Geon™ Vinyl Wire & Cable WJAX204L Polyvinyl Chloride, Flexible (PVC, Flexible)
- Polimeri Europa SINKRAL C433/M3 ABS, Heat Stabilized (discontinued **)
- Materion Brush 1915â„¢ Annealed Temper Rod
- Sumitomo Bakelite Durez® 156 Phenolic, Compression Grade
- Unifrax FyreWrap® XFP® Expanding Paper
- Chesterton ARC S7 High Temperature & Chemical Resistant Novolac Vinyl Ester Coating
- ChevronTexaco MP Drive Train Fluid
- DSM Arnite® T04 200 PBT (European Grade)
- Dow Corning 3625 A&B KIT
Copyright © lookpolymers.com All Rights Reserved