Radici Radilon® S USZ200 (dry) Nylon 6

Category	Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer	Radici Group Plastics
Trade Name
Port	Shanghai port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Radici Radilon® S USZ200 (dry) Nylon 6.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Radilon® S is a range of polyamide 6 (PA6) products obtained through the polymerization of caprolactam and used for injection, extrusion and blow-molding.Information provided by Radici group.

Physical Properties	Metric	English	Comments
Specific Gravity	1.06 g/cc	1.06 g/cc

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	35.0 MPa	5080 psi
Elongation at Break	>= 50 %	>= 50 %	Nominal
Elongation at Yield	3.5 %	3.5 %
Tensile Modulus	1.65 GPa	239 ksi
Charpy Impact Unnotched	NB <br>@Temperature 23.0 °C	NB <br>@Temperature 73.4 °F
	NB <br>@Temperature -30.0 °C	NB <br>@Temperature -22.0 °F
Charpy Impact, Notched	9.00 J/cm² <br>@Temperature 23.0 °C	42.8 ft-lb/in² <br>@Temperature 73.4 °F
	9.00 J/cm² <br>@Temperature -30.0 °C	42.8 ft-lb/in² <br>@Temperature -22.0 °F

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F
Deflection Temperature at 0.46 MPa (66 psi)	135 °C	275 °F
Deflection Temperature at 1.8 MPa (264 psi)	50.0 °C	122 °F
Vicat Softening Point	150 °C <br>@Load 5.10 kg	302 °F <br>@Load 11.2 lb	50°C/h
Flammability, UL94	HB <br>@Thickness 1.60 mm	HB <br>@Thickness 0.0630 in
	HB <br>@Thickness 0.800 mm	HB <br>@Thickness 0.0315 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+11 ohm-cm	>= 1.00e+11 ohm-cm