LG Chemical LUMID GP1300AP PA6, Plasticized
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | LG Chemical |
| Trade Name | LUMID |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUMID GP1300AP PA6, Plasticized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, PA6, PlasticizedApplication: Automotive PartsInformation provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Water Absorption | 1.7 % | 1.7 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.010 - 0.014 cm/cm @Thickness 3.20 mm |
0.010 - 0.014 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 49.0 MPa @Thickness 3.20 mm |
7110 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 250 % @Thickness 3.20 mm |
250 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 44.1 MPa @Thickness 3.20 mm |
6400 psi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| Flexural Modulus | 1.18 GPa @Thickness 3.20 mm |
171 ksi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 0.883 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
1.65 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 212 °C | 414 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C @Thickness 6.40 mm |
302 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C @Thickness 6.40 mm |
122 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.8 @Frequency 1.00e+6 Hz |
2.8 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 19.0 kV/mm @Thickness 1.00 mm |
483 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Arc Resistance | 195 sec | 195 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 215 - 250 °C | 419 - 482 °F | Injection Molding |
| Middle Barrel Temperature | 215 - 245 °C | 419 - 473 °F | Injection Molding |
| Front Barrel Temperature | 220 - 250 °C | 428 - 482 °F | Injection Molding |
| Nozzle Temperature | 220 - 250 °C | 428 - 482 °F | Injection Molding |
| Melt Temperature | 215 - 250 °C | 419 - 482 °F | Injection Molding |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Injection Molding |
| Drying Temperature | 65.0 °C | 149 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
Users viewing this material also viewed the following:
- Polimeri Europa Flexirene® MR 50 U Linear Low Density Polyethylene
- Osprey Metals T15 Tool Steel Powder (Grade 95% - 16)
- MarkeTech 97-2-1 Tungsten Alloy, AMS-T-21014 Class 4
- Silberline EternaBrite® 301-1
- DuPont™ Nomex® 410 Paper, 25.5 mil Nominal Thickness
- ExxonMobil Teresstic GT 32
- Eurotec® Tecopet® PT70 GR30 NL100 PS20 PET, 30% glass fiber reinforced, flame retardant - halogen (RoHS compliant), heat stabilized, natural, fast crystallization grade
- Braskem LF 0720/21 AF LLDPE Blown Film Extrusion Polyethylene
- Bhansali Engineering Abstron HI-34 ABS High Impact Injection Molding
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR N650 Filler
Copyright © lookpolymers.com All Rights Reserved