Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

LG Chemical LUMID GP1100A(W) PA6, Low Viscosity

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer LG Chemical
Trade Name LUMID
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUMID GP1100A(W) PA6, Low Viscosity.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Injection Molding, PA6, Low ViscosityApplication: Industrial Material, Sport PartsCAS No. 25038-54-4Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.13 g/cc
1.13 g/cc
ASTM D792
Water Absorption 1.7 %
1.7 %
ASTM D570
Linear Mold Shrinkage, Flow 0.010 - 0.014 cm/cm

@Thickness 3.20 mm
 0.010 - 0.014 in/in

@Thickness 0.126 in
 ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ASTM D785
Tensile Strength, Yield 79.4 MPa

@Thickness 3.20 mm
 11500 psi

@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break 100 %

@Thickness 3.20 mm
 100 %

@Thickness 0.126 in
 50mm/min; ASTM D638
Flexural Yield Strength 108 MPa

@Thickness 3.20 mm
 15600 psi

@Thickness 0.126 in
 2.8mm/min; ASTM D790
Flexural Modulus 2.65 GPa

@Thickness 3.20 mm
 384 ksi

@Thickness 0.126 in
 2.8mm/min; ASTM D790
Izod Impact, Notched 0.490 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
 0.918 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 80.0 µm/m-°C
44.4 µin/in-°F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 170 °C

@Thickness 6.40 mm
 338 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C

@Thickness 6.40 mm
 140 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 65.0 °C

@Thickness >=1.50 mm
 149 °F

@Thickness >=0.0591 in
65.0 °C

@Thickness >=3.00 mm
 149 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 65.0 °C

@Thickness >=1.50 mm
 149 °F

@Thickness >=0.0591 in
65.0 °C

@Thickness >=3.00 mm
 149 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 65.0 °C

@Thickness >=1.50 mm
 149 °F

@Thickness >=0.0591 in
65.0 °C

@Thickness >=7.00 mm
 149 °F

@Thickness >=0.276 in
Flammability, UL94 V-2

@Thickness >=1.60 mm
 V-2

@Thickness >=0.0630 in
V-2

@Thickness >=3.20 mm
 V-2

@Thickness >=0.126 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Dielectric Constant 3.0

@Frequency 1.00e+6 Hz
 3.0

@Frequency 1.00e+6 Hz
 ASTM D150
Dielectric Strength 19.0 kV/mm

@Thickness 1.00 mm
 483 kV/in

@Thickness 0.0394 in
 ASTM D149
Arc Resistance 195 sec
195 sec
ASTM D495
Processing Properties Metric English Comments
Rear Barrel Temperature 255 - 265 °C
491 - 509 °F
Injection Molding
Middle Barrel Temperature 230 - 260 °C
446 - 500 °F
Injection Molding
Front Barrel Temperature 240 - 270 °C
464 - 518 °F
Injection Molding
Nozzle Temperature 240 - 270 °C
464 - 518 °F
Injection Molding
Melt Temperature 240 - 270 °C
464 - 518 °F
Injection Molding
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Injection Molding
Drying Temperature 80.0 - 100 °C
176 - 212 °F
Injection Molding
Dry Time 4.00 - 5.00 hour
4.00 - 5.00 hour
Injection Molding