- SABIC Innovative Plastics NORYL LTA1350 PPE+PS (Asia Pacific)
SABIC Innovative Plastics NORYL LTA1350 PPE+PS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL LTA1350 PPE+PS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl* LTA1350 is an unfilled, injection moldable grade. Designed for improved long term heat aging, this resin also uses non-chlorinated, non-brominated FR additives to achieve a V0 UL94 rating. Noryl LTA1350 is currently available in both black and gray and may be an excellent material candidate for application requiring electrically insulating properties.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | ASTM D792 |
| Density | 1.11 g/cc | 0.0401 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.20 % | 0.20 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 10 g/10 min @Load 5.00 kg, Temperature 280 °C |
10 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Melt Index of Compound | 10 g/10 min @Load 5.00 kg, Temperature 280 °C |
10 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | Type I, 50 mm/min; ASTM D638 |
| 80.0 MPa | 11600 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | Type I, 50 mm/min; ASTM D638 |
| 83.0 MPa | 12000 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 6.0 % | 6.0 % | 50 mm/min; ISO 527 |
| 18 % | 18 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.8 % | 4.8 % | Type I, 50 mm/min; ASTM D638 |
| 5.0 % | 5.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.84 GPa | 412 ksi | 1 mm/min; ISO 527 |
| 2.85 GPa | 413 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 118 MPa | 17100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 131 MPa | 19000 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 2.77 GPa | 402 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.91 GPa | 422 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | ASTM D256 |
| 0.380 J/cm @Temperature -30.0 °C |
0.712 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 14.0 J/cm | 26.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| 3.00 kJ/m² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| 34.0 kJ/m² @Temperature -30.0 °C |
16.2 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 17.0 J @Temperature 23.0 °C |
12.5 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 83.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
46.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 83.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
46.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 89.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
49.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 89.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
49.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Hot Ball Pressure Test | <= 135 °C | <= 275 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 128 °C @Thickness 3.20 mm |
262 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 134 °C @Thickness 6.40 mm |
273 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 112 °C @Thickness 3.20 mm |
234 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| 116 °C @Thickness 6.40 mm |
241 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 135 °C | 275 °F | Rate B/50; ISO 306 |
| 137 °C | 279 °F | Rate B/120; ISO 306 | |
| 137 °C | 279 °F | Rate B/50; ASTM D1525 | |
| UL RTI, Electrical | 130 °C | 266 °F | UL 746B |
| UL RTI, Mechanical with Impact | 120 °C | 248 °F | UL 746B |
| UL RTI, Mechanical without Impact | 130 °C | 266 °F | UL 746B |
| Flammability, UL94 | V-2 @Thickness 0.750 mm |
V-2 @Thickness 0.0295 in |
UL 94 by SABIC-IP |
| V-0 @Thickness 1.00 mm |
V-0 @Thickness 0.0394 in |
UL 94 by SABIC-IP | |
| 5VA @Thickness 3.00 mm |
5VA @Thickness 0.118 in |
UL 94 by SABIC-IP | |
| Glow Wire Test | 800 °C | 1470 °F | IEC 60695-2-13 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 3.70e+16 ohm-cm | 3.70e+16 ohm-cm | ASTM D257 |
| 3.70e+16 ohm-cm | 3.70e+16 ohm-cm | IEC 60093 | |
| Surface Resistance | 4.20e+14 ohm | 4.20e+14 ohm | ASTM D257 |
| 4.20e+14 ohm | 4.20e+14 ohm | ROA; IEC 60093 | |
| Dielectric Constant | 2.7 @Frequency 1.00e+6 Hz |
2.7 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 2.76 @Frequency 1.00e+6 Hz |
2.76 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| 2.8 @Frequency 50.0 - 60.0 Hz |
2.8 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| 2.87 @Frequency 50.0 - 60.0 Hz |
2.87 @Frequency 50.0 - 60.0 Hz |
ASTM D150 | |
| Dielectric Strength | 18.6 kV/mm @Thickness 3.20 mm |
472 kV/in @Thickness 0.126 in |
in oil; ASTM D149 |
| 18.6 kV/mm @Thickness 3.20 mm |
472 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 | |
| 30.0 kV/mm @Thickness 1.50 mm |
762 kV/in @Thickness 0.0591 in |
in oil; IEC 60243-1 | |
| 30.0 kV/mm @Thickness 1.60 mm |
762 kV/in @Thickness 0.0630 in |
in oil; ASTM D149 | |
| Dissipation Factor | 0.0030 @Frequency 1.00e+6 Hz |
0.0030 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 0.0030 @Frequency 1.00e+6 Hz |
0.0030 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 0.025 @Frequency 50.0 - 60.0 Hz |
0.025 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| 0.025 @Frequency 50.0 - 60.0 Hz |
0.025 @Frequency 50.0 - 60.0 Hz |
ASTM D150 | |
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | UL 746A |
| 250 V | 250 V | IEC 60112 | |
| Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
Users viewing this material also viewed the following:
- Nabaltec APYRAL® 60CD Al(OH)3
- Greene Tweed CHEMRAZ® 639 Perfluoroelastomer
- H.C. Starck Amperit® 140.3 Tungsten (W)
- Silberline EternaBrite® 651-DL
- Denka REOMER G G5377 Thermoplastic Elastomer, For Extrusion
- ExxonMobil SAE 30 Mobilgard 300
- EMS-Griltech Grilon® TM 5100 White Nylon 6 Fiber
- Eurotec® Tecomid® NB40 NL FA50 PA6, unfilled, flame retardant - halogen free, natural
- Bhansali Engineering Abstron HI40I ABS Injection Molding Grade
- Solvay RHODAPON® LX-28/AF3 Surfactant
Copyright © lookpolymers.com All Rights Reserved