Gromax BPR20-N1 Nylon 6, Flame Retardant (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax BPR20-N1 Nylon 6, Flame Retardant (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ISO 1183 |
| Moisture Absorption | 1.30 % | 1.30 % | ISO 62 |
| Maximum Moisture Content | 0.10 | 0.10 | Karl Fischer |
| Linear Mold Shrinkage, Flow | 0.012 cm/cm | 0.012 in/in | 60x60x2 mm; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | 60x60x2 mm; ISO 294-4 |
| Melt Flow | 134 g/10 min @Load 5.00 kg, Temperature 275 °C |
134 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 75 | 75 | [N/mm<sup>2<sup>]; ISO 7619 |
| Tensile Strength | 68.6 MPa | 9960 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 15 % | 15 % | 50 mm/min; ISO 527 |
| Flexural Strength | 360 MPa | 52200 psi | 5 mm/min; ISO 178 |
| Flexural Modulus | 1.26 GPa | 182 ksi | 5 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 3.50 kJ/m² | 1.67 ft-lb/in² | ISO 180-1A |
| Charpy Impact Unnotched | 0.400 J/cm² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU |
| Charpy Impact, Notched | 5.50 J/cm² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75-1,-2 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | ISO 294 |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | ISO 294 |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour |
Users viewing this material also viewed the following:
- Multibase Nylex™ 2185 NAT Polyamide + PP
- Orion Engineered Carbons CORAX® N 774 ASTM Carbon Black
- 3M Dyneon™ THV 340C Fluorothermoplastic (discontinued **)
- Teknor Apex APEX® RE 9016A Polyvinyl Chloride, Rigid
- A. Schulman SCHULAMID® 66 GF33H 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66
- ExxonMobil LD 302.20 High Clarity, High Impact Film Resin
- Eurotec® Tecoform® PO20 GR25 NL HS POM, 25% glass fiber reinforced, heat stabilized, natural
- 3M 5491 PTFE Extruded Film Tape
- Addiplast Addilene PMD 50218 Flame Retardant Polypropylene
- Polymer Resources PPX-FR4 Modified PPO, UL 94 V-1 with HDT of 185 F (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved