- Nilit FRIANYL B63 SG30 Nylon 6 for injection molding, 30% mineral filled
Nilit FRIANYL B63 SG30 Nylon 6 for injection molding, 30% mineral filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Mineral Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 SG30 Nylon 6 for injection molding, 30% mineral filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 |
| Water Absorption | 1.5 - 2.5 % | 1.5 - 2.5 % | ISO 62 |
| Water Absorption at Saturation | 6.0 - 7.0 % | 6.0 - 7.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0090 - 0.019 cm/cm | 0.0090 - 0.019 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 150 MPa | 21800 psi | ISO 2039-1 |
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ISO 527 |
| Elongation at Break | 30 % | 30 % | ISO 527 |
| Tensile Modulus | 3.50 GPa | 508 ksi | ISO 527 |
| Flexural Strength | 85.0 MPa | 12300 psi | ISO 178 |
| Flexural Modulus | 3.10 GPa | 450 ksi | ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| NB | NB | DIN 53453 | |
| NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179/1eA |
| 1.00 J/cm² | 4.76 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 100 °C | 212 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 450 V | 450 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Polymer Resources TP-FR-IM2 Polybutylene Terephthalate, Impact Modified, Flame Retardant, High Flow
- Lanxess Durethan® AM 40 X H2.0 901510 Nylon 66, Glass Fiber/Mineral Reinforced
- Indium Corp. Indalloy® 2 In-Pb-Ag Solder Alloy
- Techmer ES Elastoblend® PA6 GF40 IM2 NAT 40% Glass Filled
- Sumitomo Chemical ESPOLEX® WT361 Thermoplastic Elastomer
- SABIC Innovative Plastics NORYL BN31 PPE+PS
- 3M 9018FL Screen Printable Sheet Polyester Label Material
- ExxonMobil Escorene® Escomer® H-101 Low MW HDPE Wax (discontinued **)
Copyright © lookpolymers.com All Rights Reserved