LG Chemical KEYFLEX BT 1045D Ester Type TPE
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | LG Chemical |
| Trade Name | KEYFLEX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical KEYFLEX BT 1045D Ester Type TPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, TPC-ET, General Purpose, Medium ModulusApplication: Antenna Cover, Injection Parts for Leisure & SportsCAS: 37282-12-5Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Water Absorption | 0.60 % @Temperature 23.0 °C, Time 86400 sec |
0.60 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Molecular Weight | 458.458 g/mol | 458.458 g/mol | |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| 0.010 | 0.010 | Extrusion Molding | |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.010 cm/cm @Thickness 3.20 mm |
0.0060 - 0.010 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 25 g/10 min @Load 2.16 kg, Temperature 200 °C |
25 g/10 min @Load 4.76 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 95 | 95 | ASTM D2240 |
| Hardness, Shore D | 42 | 42 | ASTM D2240 |
| Tensile Strength at Break | 27.5 MPa @Thickness 2.00 mm |
3990 psi @Thickness 0.0787 in |
50mm/min; ASTM D638 |
| Elongation at Break | 650 % @Thickness 2.00 mm |
650 % @Thickness 0.0787 in |
50mm/min; ASTM D638 |
| Flexural Modulus | 0.0785 GPa @Thickness 6.40 mm |
11.4 ksi @Thickness 0.252 in |
15mm/min; ASTM D790 |
| Izod Impact, Notched | NB @Thickness 6.40 mm, Temperature 23.0 °C |
NB @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| NB @Thickness 6.40 mm, Temperature -40.0 °C |
NB @Thickness 0.252 in, Temperature -40.0 °F |
ASTM D256 | |
| Tear Strength | 123 kN/m | 700 pli | 50mm/min, at Break; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 180 °C | 356 °F | Peak |
| Boiling Point | 140 - 230 °C | 284 - 446 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 65.0 °C @Thickness 6.40 mm |
149 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Flash Point | 300 - 340 °C | 572 - 644 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | ASTM D257 |
| Dielectric Strength | 26.0 kV/mm @Thickness 1.00 mm |
660 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 180 - 200 °C | 356 - 392 °F | Injection Molding |
| Middle Barrel Temperature | 190 - 210 °C | 374 - 410 °F | Injection Molding |
| Front Barrel Temperature | 200 - 220 °C | 392 - 428 °F | Injection Molding |
| Nozzle Temperature | 200 - 220 °C | 392 - 428 °F | Injection Molding |
| Zone 1 | 180 - 200 °C | 356 - 392 °F | Extrusion Molding |
| Zone 2 | 190 - 210 °C | 374 - 410 °F | Extrusion Molding |
| Zone 3 | 200 - 220 °C | 392 - 428 °F | Extrusion Molding |
| Zone 4 | 200 - 220 °C | 392 - 428 °F | Extrusion Molding |
| Adapter Temperature | 200 - 220 °C | 392 - 428 °F | Extrusion Molding |
| Die Temperature | 190 - 230 °C | 374 - 446 °F | Extrusion Molding |
| Melt Temperature | 180 - 220 °C | 356 - 428 °F | Injection Molding |
| 180 - 220 °C | 356 - 428 °F | Extrusion Molding | |
| Mold Temperature | 10.0 - 35.0 °C | 50.0 - 95.0 °F | Injection Molding |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection Molding |
| 80.0 - 90.0 °C | 176 - 194 °F | Extrusion Molding | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| 3.00 - 4.00 hour | 3.00 - 4.00 hour | Extrusion Molding |
Users viewing this material also viewed the following:
- LATI LATAN 3E71 Polyoxymethylene Copolymer (POM) with Elastomer (Unverified Data**)
- 3M Dyneon™ TF 5033 PTFE Dispersion (discontinued **)
- Greene Tweed Arlon® 1260 Polyketone, Carbon Filled
- Schott P-SF8 Glass
- Saint-Gobain Norton® T-200 Mechanical Grade PTFE Sheet (0.031" thick)
- Williams Advanced Alloys WS221 Solder
- Braskem LF0720/21AF Blown Film Extrusion Linear Low Density Polyethylene
- BASF Capron® 8360 HS 34% Mineral-Filled Nylon 6 (Dry) (discontinued **)
- ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 305, 0% Cold Rolled (UNS S30500)
Copyright © lookpolymers.com All Rights Reserved