PolyOne Nymax™ GF 600 A 33 Natural Polyamide 6 (Nylon 6)

Category	Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer	PolyOne Corporation
Trade Name	Nymax™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Nymax™ GF 600 A 33 Natural Polyamide 6 (Nylon 6).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

The Nymax® GF 600 Series of glass fiber-reinforced nylon 6 compounds have been specifically engineered for applications requiring high stiffness, tensile strength, and toughness, while providing enhanced surface appearance versus nylon 6/6 compounds. These materials are available in a broad range of reinforcement levels depending upon stiffness characteristics desired and have been formulated to offer ease of processing in most standard thermoplastic processing equipment.Molded Test Bars: Dry as MoldedInformation provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.36 g/cc	1.36 g/cc	ASTM D792
Density	1.40 g/cc	0.0506 lb/in³	ISO 1183
Water Absorption	0.81 %	0.81 %	24h/23C; ISO 62
	1.0 % @Thickness 3.18 mm	1.0 % @Thickness 0.125 in	@ 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow	0.0020 cm/cm	0.0020 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	182 MPa	26400 psi	ISO 527
Tensile Strength, Yield	165 MPa	23900 psi	Type I, 5.1 mm/min; ASTM D638
Elongation at Break	12 %	12 %	ISO 527
Elongation at Yield	4.0 %	4.0 %	Type I, 5.1 mm/min; ASTM D638
Flexural Strength	241 MPa	35000 psi	ASTM D790
	242 MPa	35100 psi	ISO 178
Flexural Modulus	8.27 GPa	1200 ksi	ASTM D790
	9.31 GPa	1350 ksi	ISO 178
Izod Impact, Notched	1.30 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	2.44 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256A
Izod Impact, Notched (ISO)	15.0 kJ/m²	7.14 ft-lb/in²	Partial Break; ISO 180

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	ASTM D789
Deflection Temperature at 0.46 MPa (66 psi)	220 °C @Thickness 3.18 mm	428 °F @Thickness 0.125 in	Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	202 °C	396 °F	Annealed; ISO 75-2/A
	206 °C @Thickness 3.18 mm	403 °F @Thickness 0.125 in	Annealed; ASTM D648

Processing Properties	Metric	English
Mold Temperature	48.9 - 93.3 °C	120 - 200 °F
Drying Temperature	82.2 °C	180 °F
Dry Time	4.00 hour	4.00 hour

Descriptive Properties	Value	Comments
Appearance	Natural Color
Automotive Specifications	CHRYSLER MS-DB41 CPN2625 Color: 100% Color Match
	CHRYSLER MS-DB41 CPN4338 Color: Non-matched Color
Features	General Purpose
Filler / Reinforcement	Glass Fiber Reinforcement, 33% Filler by Weight
Forms	Pellets
Generic Material	Nylon 6
Generic Name	Polyamide 6 (Nylon 6)
Processing Method	Injection Molding
Regional Availability	North America
	South America
Uses	Automotive Applications
	Construction Applications
	Consumer Applications
	General Purpose
	Industrial Applications