- Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
- LG Chemical BM662 ABS, Heat Resistance
LG Chemical BM662 ABS, Heat Resistance
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | LG Chemical |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical BM662 ABS, Heat Resistance.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Blow Molding, Heat ResistanceApplication: Automotives Exterior Housing (Spoiler, Bumper Guard etc.)CAS No. 25120-20-1, 9003-56-9, 25747-74-7 and 9003-54-7Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Blow Molding |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 4.4 g/10 min @Load 10.0 kg, Temperature 220 °C |
4.4 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 102 | 102 | ASTM D785 |
| Tensile Strength, Yield | 46.1 MPa @Thickness 3.20 mm |
6680 psi @Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Elongation at Break | 20 % @Thickness 3.20 mm |
20 % @Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Flexural Yield Strength | 71.6 MPa @Thickness 3.20 mm |
10400 psi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
| Flexural Modulus | 2.26 GPa @Thickness 3.20 mm |
327 ksi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.96 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
3.67 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| 2.16 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
4.04 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 0.981 J/cm @Thickness 6.40 mm, Temperature -30.0 °C |
1.84 ft-lb/in @Thickness 0.252 in, Temperature -22.0 °F |
ASTM D256 |
| 0.981 J/cm @Thickness 3.20 mm, Temperature -30.0 °C |
1.84 ft-lb/in @Thickness 0.126 in, Temperature -22.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C @Thickness 6.40 mm |
212 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C @Thickness 6.40 mm |
199 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Vicat Softening Point | 100 °C @Load 5.00 kg |
212 °F @Load 11.0 lb |
50°C/h; ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 180 - 200 °C | 356 - 392 °F | Blow Molding |
| Zone 2 | 190 - 210 °C | 374 - 410 °F | Blow Molding |
| Zone 3 | 190 - 210 °C | 374 - 410 °F | Blow Molding |
| Zone 4 | 200 - 220 °C | 392 - 428 °F | Blow Molding |
| Adapter Temperature | 220 °C | 428 °F | Blow Molding |
| Die Temperature | 220 °C | 428 °F | Blow Molding |
| Melt Temperature | 200 - 210 °C | 392 - 410 °F | Blow Molding |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Blow Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Blow Molding |
Users viewing this material also viewed the following:
- NOVA Chemicals EPS 34RB Regular Expandable Polystyrene
- MBA Polymers PS 3122 Post-consumer recycled impact modified polystyrene
- Shandong Dongyue Shenzhou New Material Co CHF100 Perfluorosulfonic Acid Ion-Exchange Resin (PFSA)
- Unitika A3030N-2 PA6, 30% Mineral Reinforced, Dry
- Wellman Wellamid® MR409 22H-GY1 Nylon 66, 40% Mineral Reinforced
- ExxonMobil Mobilarma 778
- TSE Industries Millathane® 66 Millable Polyurethane Rubber
- BASF Ultrason® P 3010 PPSU Unreinforced Polyphenylsulfone
- Overview of materials for Polyethylene Terephthalate (PET), Unreinforced
Copyright © lookpolymers.com All Rights Reserved