BLUESTAR LXS 314 G30 PPE-HIPS, 30% Glass Filled
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) , Polystyrene + Polyphenylene Ether, Glass Filler |
| Manufacturer | BLUESTAR |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BLUESTAR LXS 314 G30 PPE-HIPS, 30% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Typical Applications: Water industrial partsInformation provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D792 |
| Water Absorption | 0.10 % @Temperature 23.0 °C, Time 86400 sec |
0.10 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D955 |
| Melt Flow | 15 g/10 min @Load 5.00 kg, Temperature 300 °C |
15 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 110 MPa | 16000 psi | type I; ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | type I; ASTM D638 |
| Flexural Strength | 160 MPa | 23200 psi | 2.6 mm/min; ASTM D790 |
| Flexural Modulus | 5.50 GPa | 798 ksi | 2.6 mm/min; ASTM D790 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C @Thickness 6.40 mm |
275 °F @Thickness 0.252 in |
ASTM D648 |
Users viewing this material also viewed the following:
- NEU NeuSoft™ 597-60A Industrial Ether TPU / SBC blend
- Gouda Vuurvast CURON 160 HS GM Dense Refractory Castable
- Multibase C6-235 PERKADOX PD-50S Dow-Corning Class VI Elastomer
- UBE PAE1200U2 Electronic Grade Nylon Elastomer
- A. Schulman POLYBATCH™ Green P30244/4 Concentrate Based In Copolymer PP
- Chevron Phillips K-Resin® KR52 Styrene-Butadiene Copolymer
- Fainplast Compounds Hax™ HF 039/4H Flame Retardant Polyolefin Cable Compound
- Azoty Tarnow™ Alphalon™ E 36 L Nylon 6
- Beijing Ranger Chem 0164P Liquid Epoxy Resin
Copyright © lookpolymers.com All Rights Reserved