LATI Latene® EP 7-V2 PP Copolymer, Flame Retardant
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant |
| Manufacturer | LATI |
| Trade Name | Latene® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latene® EP 7-V2 PP Copolymer, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polypropylene copolymer (PPc) based compound. UL94 V-2 classified, with brominated flame retardants, PBB/PBDE free. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.014 - 0.017 cm/cm | 0.014 - 0.017 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0145 - 0.0175 cm/cm | 0.0145 - 0.0175 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Elongation at Break | >= 100 % @Temperature 23.0 °C |
>= 100 % @Temperature 73.4 °F |
|
| >= 100 % @Temperature 60.0 °C |
>= 100 % @Temperature 140 °F |
||
| >= 100 % @Temperature 90.0 °C |
>= 100 % @Temperature 194 °F |
||
| Elongation at Yield | 6.0 % @Temperature 23.0 °C |
6.0 % @Temperature 73.4 °F |
|
| 9.0 % @Temperature 60.0 °C |
9.0 % @Temperature 140 °F |
||
| 9.0 % @Temperature 90.0 °C |
9.0 % @Temperature 194 °F |
||
| Tensile Modulus | 0.350 GPa @Temperature 90.0 °C |
50.8 ksi @Temperature 194 °F |
|
| 0.600 GPa @Temperature 60.0 °C |
87.0 ksi @Temperature 140 °F |
||
| 1.35 GPa @Temperature 23.0 °C |
196 ksi @Temperature 73.4 °F |
||
| Charpy Impact Unnotched | 10.0 J/cm² @Temperature -20.0 °C |
47.6 ft-lb/in² @Temperature -4.00 °F |
|
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
||
| Charpy Impact, Notched | 0.300 J/cm² @Temperature -20.0 °C |
1.43 ft-lb/in² @Temperature -4.00 °F |
|
| 0.800 J/cm² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 75.0 °C | 167 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | |
| Vicat Softening Point | 70.0 °C @Load 5.00 kg |
158 °F @Load 11.0 lb |
|
| Flammability, UL94 | V-2 @Thickness 1.50 mm |
V-2 @Thickness 0.0591 in |
|
| Oxygen Index | 25 % | 25 % | |
| Glow Wire Test | 960 °C @Thickness 1.00 mm |
1760 °F @Thickness 0.0394 in |
GWFI/GWT |
| 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
GWFI/GWT |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | A solution |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 - 210 °C | 356 - 410 °F | |
| Mold Temperature | 20.0 - 40.0 °C | 68.0 - 104 °F | |
| Drying Temperature | 80.0 - 90.0 °C @Time 10800 sec |
176 - 194 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- Nyco M3 WOLLASTOCOAT® Wollastonite
- PolyOne Versaflex™ 9570-1 Thermoplastic Elastomer (TPE)
- SABIC Innovative Plastics Geloy HRA222 ASA (Europe-Africa-Middle East)
- SABIC Innovative Plastics Lexan® EXL8483 PC COPOLYMER (Asia Pacific)
- SGL Carbon Group PANOX® LB S004 EEA Oxidized Textile Fiber, Staple Fiber, For carbon/carbon and spinning
- Special Metals INCONEL® C276 Nickel Superalloy Tubing, 0% Cold Work (Annealed)
- Schott OG550 Long Pass Filter
- Hexcel® HexPly® F263 Epoxy Resin, T3T145 Carbon Tape
- 3M 1182 EMI Shielding Tape
Copyright © lookpolymers.com All Rights Reserved