SABIC Innovative Plastics LNP LUBRICOMP RCL34 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RCL34 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* RCL34 is a compound based on Nylon 66 containing 20% Carbon Fiber, 15% PTFE. Added features of this grade includes: Wear Resistant, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D792 |
| Density | 1.33 g/cc | 0.0480 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.670 % | 0.670 % | 50% RH, 24 hrs; ASTM D570 |
| 0.950 % | 0.950 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 211 MPa | 30600 psi | 5 mm/min; ISO 527 |
| 215 MPa | 31200 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.4 % | 2.4 % | 5 mm/min; ISO 527 |
| 2.6 % | 2.6 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 16.33 GPa | 2368 ksi | 1 mm/min; ISO 527 |
| 16.54 GPa | 2399 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 296 MPa | 42900 psi | ISO 178 |
| 312 MPa | 45300 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 12.83 GPa | 1861 ksi | 2 mm/min; ISO 178 |
| 13.2 GPa | 1910 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.00 J/cm | 1.87 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.93 J/cm | 14.9 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 52.0 kJ/m² | 24.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.40 | 0.40 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.34 | 0.34 | ASTM D3702 Modified |
| K (wear) Factor | 48.3 x 10-8 mm³/N-M | 24.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
5.56 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 61.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
33.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 261 °C | 502 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 262 °C @Thickness 3.20 mm |
504 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 251 °C | 484 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 255 °C @Thickness 3.20 mm |
491 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 5 T 20 FRG 2 PA6, 5% glass fibre, 20% mineral filling
- Kuraray SEPTON® S8006 Thermoplastic Rubber
- SABIC Innovative Plastics LNP LUBRICOMP PFL38S PA 6
- Saint-Gobain Norton® T-100 Virgin Skived PTFE Film (0.002" thick)
- Ter Hell Plastic Terez® PA/PP 7500 GF 7/1 Polyamide/Polypropylene
- Chesterton MRS S4+ Metal Rebuilding System
- DSM Akulon® K223-HM6 (BLACK) Nylon 6-30% Mineral Reinforced (European and Asian Grade) (Cond)
- China Tungsten YG11X Tungsten Carbide Powder
- Polyram RamSter PF303G4 PBT, 20% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved