LATI Latan 13 G/30 POM, 30% Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 30% Glass Fiber Reinforced |
| Manufacturer | LATI |
| Trade Name | Latan |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latan 13 G/30 POM, 30% Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyoxymethylene (POM) based compound. Glass fibers. Medium viscosity. Good tribological properties.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0045 - 0.0070 cm/cm | 0.0045 - 0.0070 in/in | |
| Linear Mold Shrinkage, Transverse | 0.011 - 0.014 cm/cm | 0.011 - 0.014 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa @Temperature 90.0 °C |
7980 psi @Temperature 194 °F |
|
| 85.0 MPa @Temperature 60.0 °C |
12300 psi @Temperature 140 °F |
||
| 100 MPa @Temperature 23.0 °C |
14500 psi @Temperature 73.4 °F |
||
| Elongation at Break | 3.0 % @Temperature 23.0 °C |
3.0 % @Temperature 73.4 °F |
|
| 4.0 % @Temperature 60.0 °C |
4.0 % @Temperature 140 °F |
||
| 5.8 % @Temperature 90.0 °C |
5.8 % @Temperature 194 °F |
||
| Tensile Modulus | 4.00 GPa @Temperature 90.0 °C |
580 ksi @Temperature 194 °F |
|
| 5.90 GPa @Temperature 60.0 °C |
856 ksi @Temperature 140 °F |
||
| 7.50 GPa @Temperature 23.0 °C |
1090 ksi @Temperature 73.4 °F |
||
| Charpy Impact Unnotched | 2.50 J/cm² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
|
| Charpy Impact, Notched | 0.500 J/cm² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 85.0 °C | 185 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | |
| Vicat Softening Point | 150 °C @Load 5.00 kg |
302 °F @Load 11.0 lb |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | A solution |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 - 210 °C | 356 - 410 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 80.0 - 90.0 °C @Time 10800 sec |
176 - 194 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- Osprey Metals Ni40Cu Binary Alloy Powder (Grade 80% - 22)
- PolyOne Dynaflex™ G7630-9 (Black) Thermoplastic Elastomer (TPE)
- Michelman® Michem® Emulsion 66035 Anionic paraffin/polyethylene wax emulsion
- Menzolit Menzolit® SMC 0300 Unsaturated Polyester UP
- International Mold Steel TOOLOX 44® Plastic and Rubber Mold Steel
- SABIC Innovative Plastics NORYL EFN4230 PPE+PS (Asia Pacific)
- A. Schulman POLYFORT™ FXP 1943 CaC03 and Glass Fiber Hybrid Copolymer Polypropylene
- Dow Nordel® IP 4520 Molded Golf Grip
- DuPont Performance Polymers Hytrel® G3548L TPC-ET (Unverified Data**)
- Carmel Olefins CAPILENE® HT 75 A Polypropylene Impact Copolymer
Copyright © lookpolymers.com All Rights Reserved