Aclo Accutech Polypropylene Copolymer CP0436W20L1 Wollastonite Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Copolymer CP0436W20L1 Wollastonite Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | MD; ASTM D955 |
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Ash | 20 % | 20 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 59 | 59 | ASTM D785 |
| Tensile Strength at Break | 15.0 MPa | 2180 psi | ASTM D638 |
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | ASTM D638 |
| Elongation at Break | 32 % | 32 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 1.80 GPa | 261 ksi | ASTM D638 |
| Flexural Strength | 25.0 MPa | 3630 psi | ASTM D790 |
| Flexural Modulus | 1.550 GPa | 224.8 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm | 2.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C | 216 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 56.1 °C | 133 °F |
Users viewing this material also viewed the following:
- Orion Engineered Carbons ECORAX® 1720 Carbon Black
- Premix Thermoplastics PREFLEX E100 Polyphenylene Ether (PPO/PPE)
- LG Chemical LUCEL HI-515 High Impact POM, Unreinforced
- Styrolution PS 486N HIPS
- Sumitomo Chemical Sumipex® BF3 Acrylic Resin, GP Blow Molding Grade
- Teknor Apex Monprene® MP 1672 Thermoplastic Elastomer
- Chase Plastics CP Pryme® NN100TL (Dry) Nylon 66, Lubricated, Impact Modified
- Chase Plastics CP Pryme® NN133L (Dry) Nylon 66, 33% Glass Fiber Reinforced, Lubricated
- Beijing Chemical Industry KAIFA® 551GT20S PBT Resin
- Pau Tai Avanstab TM-3820 Organotin Stabilizer Butyl Thiotin
Copyright © lookpolymers.com All Rights Reserved