Malvern Minerals Sliastic 437 with 50% Novacite® Daper Quartz Filler
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) , Silicone , Silicone Rubber |
| Manufacturer | Malvern Minerals Company |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Malvern Minerals Sliastic 437 with 50% Novacite® Daper Quartz Filler.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Press Vulcanized 5 minutes at 260° F. Product data demonstrates the effect of the Novacite® filler.Information provided by Malvern Minerals Company.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 53 | 53 | Oven cured 4 hours at 480°F |
| 55 | 55 | Heat Aged 24 hours at 600F | |
| Tensile Strength at Break | 3.72 MPa | 540 psi | Heat Aged 24 hours at 600F |
| 5.52 MPa | 800 psi | Oven cured 4 hours at 480°F | |
| Elongation at Break | 200 % | 200 % | Heat Aged 24 hours at 600F |
| 310 % | 310 % | Oven cured 4 hours at 480°F | |
| Tear Strength | 13.7 kN/m | 78.0 pli | Die B |
Users viewing this material also viewed the following:
- Performance Polymers IPS II PPL-C4150 PEKK (Polyetherketoneketone) Linear 30 % Glass Fiber Reinforced Molding Grade
- PolyOne Edgetek® AS-10GF/000 FR Acrylonitrile Butadiene Styrene (ABS), Glass/Carbon Fiber Filled (discontinue
- Lehmann & Voss LUVOCOM® 1106-7622 Polyether imide, with carbon fiber
- SCG Chemicals EL-Leneâ„¢ LD2305F Low Density Polyethylene Film
- SABIC Innovative Plastics NORYL GTX GTX810 PPE+PA (Europe-Africa-Middle East)
- Tipco Tipcolite® TG 618 Phenolic Compound, Mineral & Wood Flour, Medium Flow & High Electrical Properties
- Hexcel® IM4 Carbon Fiber (12,000 Filaments)
- BorsodChem ONGROSTYR F-I Expandable Polystyrene (EPS)
- BASF Ultradur® S 4090 GX 14% Glass Filled PBT
Copyright © lookpolymers.com All Rights Reserved