- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 165 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 165 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) |
165
°C <br>@Thickness 3.18 mm
|
329
°F <br>@Thickness 0.125 in
|
Unannealed; ASTM D648 |
|
PolyOne Nymax™ 600 A HS Natural A Polyamide 6 Alloy (Nylon 6 Alloy)
The Nymax® 600 Blend Series of nylon 6 materials are salt-and-pepper pelletized blends combining select nylon resins and process aids, performance modifiers, and color concentrates. These materials..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | DIN 53461; ASTM D648 |
|
Kolon SPESIN® KP212VO Flame Retardant PBT Resin
(discontinued **)
SPESIN® is a thermoplastic PBT resin with excellent thermal, mechanical and electrical properties. SPESIN® is widely used in industrial parts and especially in electrical-electronic parts.High hea..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75-1/-2 |
|
DuPont Performance Polymers Delrin® FG500TL NC010 Acetal Homopolymer
(Unverified Data**)
Delrin® FG500TL medium viscosity acetal homopolymer resin containing 1.5% Teflon® PTFE Micropowder. It has been developed for consideration into applications such as parts for the food industry.In..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ASTM D648 |
|
Asahi Kasei Tenac® LA531 Acetal Homopolymer, High Lubricity
(discontinued **)
High-lubricity block copolymer with excellent friction and wear characteristics, especially on POM.Applications: Gears, keyboard parts.This product is not a part of the standard product line dated 2..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ASTM D648 |
|
LATI LATAN 13 G/15 15% Glass Fiber Reinforced Polyoxymethylene Copolymer (POM)
(discontinued **)
Description: Latan series thermoplastics are polyoxymethylene copolymer (POM) products. The main applications for Latan feature good wear resistance, chemical inertness and low water absorption (gea..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
165
°C <br>@Thickness 6.40 mm
|
329
°F <br>@Thickness 0.252 in
|
Unannealed; ASTM D648 |
|
LG Chemical LUCEL GC210 POM+GF10%, High Rigidity
Feature: Injection Molding, POM+GF10%, High RigidityApplication: Casings of Pump and Pivot BearingsCAS No. 66455-31-0 and 65997-17-3Information provided by LG Chemical
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
165
°C <br>@Thickness 6.40 mm
|
329
°F <br>@Thickness 0.252 in
|
Unannealed; ASTM D648 |
|
LG Chemical LUCEL GC225 POM+GF25%, High Rigidity
Feature: Injection Molding, POM+GF25%, High RigidityApplication: Casings of Pump and Pivot BearingsCAS No. 66455-31-0 and 65997-17-3Information provided by LG Chemical
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ASTM D648 |
|
LG Chemical LUCEL MR-320 Low Warpage POM, 20% Mineral Filled
LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ASTM D648 |
|
Gromax PBT 2000-104D
Product Description: PBT unreinforced injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature. Excellent mechanic an..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ASTM D648 |
|
Gromax PBT 2000-201D
Product Description: PBT unreinforced injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature. Excellent mechanic an..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | |
|
LATI Latan 13 G/30 POM, 30% Glass Fiber Reinforced
Polyoxymethylene (POM) based compound. Glass fibers. Medium viscosity. Good tribological properties.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | |
|
LATI Latiohm 73-09 PD01 G/20 POM, 20% Glass Fiber Reinforced
Semiconductive/dissipative product based on Polyoxymethylene (POM). Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | |
|
LATI Latiohm 90/13-09 PD01 G/10 PPOm, 10% Glass Fiber Reinforced
Semiconductive/dissipative product based on Modified Polyphenylene Oxide (PPOm). Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation prov..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
165
°C <br>@Thickness 3.20 mm
|
329
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP KFL32R Acetal Copolymer
LNP LUBRICOMP* KFL32R is a compound based on Acetal Copolymer resin containing 10% Glass Fiber, 15% PTFE. Added feature of this material is: Easy Release, Wear Resistant.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
165
°C <br>@Thickness 3.20 mm
|
329
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP 5C003 FP-V (PVDF)
LNP THERMOCOMP* 5C003 is a compound based on Polyvinylidene Fluoride resin containing 15% Carbon Fiber. Added features of this material include: Electrically Conductive.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP Thermocomp WB008 PBT
LNP* Thermocomp* WB008 is a compound based on Thermoplastic Polyester (PBT) containing Glass Beads.This data was supplied by SABIC-IP for the Americas region.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | no load specified; ASTM D648 |
|
Formosa Plastics Formolon® AW02 Homopolymer/Compound
Homopolymer/Compound Formolon (AW02) is a NSF approved medium molecular weight dry blend PVC compound. This compound has been engineered primarily for rigid extrusion applications. The exceptional ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75-1/-2 |
|
DuPont Performance Polymers Delrin® 300CP NC010 Acetal (POM)
(Unverified Data**)
Medium-high Viscosity Acetal Homopolymer with Improved ProcessingDelrin 300CP is a medium-high viscosity acetal homopolymer with improved thermal stability and an outstanding balance of ease of proc..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75-1/-2 |
|
DuPont Performance Polymers Delrin® FG500TL NC010 Acetal (POM)
(Unverified Data**)
Teflon® Lubricated Medium Viscosity Acetal Homopolymer with Low Wear and Low Friction Developed for Food Contact ApplicationsDelrin FG500TL medium viscosity acetal homopolymer resin containing 1.5%..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75-1/-2 |
|
DSM Arnite® T06 200 (extrusion) PBT (European and Asian Grade)
Arnite resins are engineered to provide specific performance in applications where DSM technology can offer value.Arnite Molding resins: Standard Unfilled and Reinforced materialsHigh modulus Flame ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75 |
|
Eurotec® Tecodur® PB70 NL XA20 PBT, flame retardant - halogen (RoHS compliant), heat stabilized, natural
Information provided by Eurotec®
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75-2 |
|
BASF Ultradur B 2550 PBT
Ultradur B2550 is an unfilled, very free-flowing grade for coating paper and board with high heat resistance, for example for packaging of frozen goods and ready-prepared meals. Also suitable for in..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75 |
|
BASF Ultramid® 8202C HS PA6 (Dry)
Ultramid 8202C HS is a heat stabilized, low viscosity, PA6 injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It is also..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75 -1 & -2 flat |
|
Asahi Kasei Tenac® 4010 Homopolymer Acetal Resin
General purpose grade, high impact, high elongation, medium viscosityInformation provided by Asahi Kasei Corporation.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75-1/-2 |
|
DuPont Performance Polymers Delrin® FG150 NC010 Acetal Homopolymer
(Unverified Data**)
Delrin® FG150 NC010 is a high viscosity acetal homopolymer for extrusion processes. It has low die deposit and low porosity. It has been developed for consideration in applications and parts for th..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75 -1 & -2 flat |
|
Asahi Kasei Tenac® SH410 Homopolymer Acetal Resin
General purpose grade, high impact, high elongation, medium viscosityInformation provided by Asahi Kasei Corporation.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | |
|
LATI Later 4 PBT
Polybutylene Terephthalate (PBT). Unfilled. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ASTM D648 |
|
Chang Chun Plastic PBT2000 Fire Retardant PBT
Information provided by Dowell Trading Company Ltd.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75-1/-2 |
|
DSM Arnite® T06 204 SN PBT (European and Asian Grade)
Arnite resins are engineered to provide specific performance in applications where DSM technology can offer value.Arnite Molding resins: Standard Unfilled and Reinforced materialsHigh modulus Flame ..
|
|||