Solvay Specialty Polymers Ajediumâ„¢ PVDF 9009 Polyvinylidene Fluoride (PVDF)
| Category | Polymer , Film , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Ajedium™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Ajediumâ„¢ PVDF 9009 Polyvinylidene Fluoride (PVDF).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Solef® 9009 PVDF homopolymer is a semi-crystalline fluoropolymer. Solef® film is chemically inert to most acids, aliphatic and aromatic organic compounds, chlorinated solvents and alcohols.Features: HomopolymerAdditional Properties: Area Factor - 108 ft²/lb/milInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.75 - 1.80 g/cc | 0.0632 - 0.0650 lb/in³ | ASTM D792 |
| Water Absorption | <= 0.040 % @Time 86400 sec |
<= 0.040 % @Time 24.0 hour |
ISO 62 |
| Thickness | 25.0 microns | 0.984 mil | As Tested |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 55.0 MPa | 7980 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 56.0 MPa | 8120 psi | ASTM D882 |
| Film Elongation at Break, MD | 200 % | 200 % | ASTM D882 |
| Film Elongation at Break, TD | 250 % | 250 % | ASTM D882 |
| Film Elongation at Yield, MD | 6.0 % | 6.0 % | ASTM D882 |
| Film Elongation at Yield, TD | 6.2 % | 6.2 % | ASTM D882 |
| Secant Modulus, MD | 2.00 GPa | 290 ksi | ASTM D882 |
| Secant Modulus, TD | 2.10 GPa | 305 ksi | ASTM D882 |
| Coefficient of Friction, Dynamic | 0.15 - 0.35 | 0.15 - 0.35 | vs. Itself; ASTM D1894 |
| Coefficient of Friction, Static | 0.20 - 0.40 | 0.20 - 0.40 | vs. Itself; ASTM D1894 |
| Taber Abrasion, mg/1000 Cycles | 5.0 - 10 | 5.0 - 10 | CS-10 Wheel, 1000 g; ASTM D1044 |
| Film Tensile Strength at Break, MD | 57.0 MPa | 8270 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 54.0 MPa | 7830 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 140 µm/m-°C | 77.8 µin/in-°F | |
| Specific Heat Capacity | 1.60 J/g-°C @Temperature 100 °C |
0.382 BTU/lb-°F @Temperature 212 °F |
ASTM C351 |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 162 - 168 °C | 324 - 334 °F | DSC |
| Crystallization Temperature | 133 - 140 °C | 271 - 284 °F | Peak; ASTM D3418 |
| Glass Transition Temp, Tg | -40.0 °C | -40.0 °F | ASTM E1356 |
| Oxygen Index | 44 % @Thickness 3.00 mm |
44 % @Thickness 0.118 in |
ASTM D2863 |
| Shrinkage | 0.70 % @Temperature 130 °C |
0.70 % @Temperature 266 °F |
Free Shrinkage; ASTM D2732 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 |
| Dielectric Constant | 7.5 | 7.5 | ASTM D150 |
| Dielectric Strength | 20.0 - 25.0 kV/mm @Thickness 1.00 mm |
508 - 635 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Asia Pacific | |
| Europe | ||
| Latin America | ||
| North America |
Users viewing this material also viewed the following:
- PolyOne Edgetek® AT-30GF/000 FDA Acetal-Copolymer, Glass Filled (discontinued **)
- Overview of materials for Nylon 6, Glass/Mineral Reinforced
- Sharadaa Ceramics PCF70 (M) Precast Prefired Brick
- Techmer ES HiFill® PA6/6 E4 HS MB Nylon 66
- CRP Technology Windform® GT Polyamide Glass Composite
- Akzo Nobel Expancel® 950 DU 80 Dry unexpanded microspheres
- Aremco Ceramabond™ 552 High Temperature Ceramic Adhesive/Paste, Alumina Filled
- ATI Allegheny Ludlum AL Altemp® 625 Nickel-Base Superalloy, UNS N06625
Copyright © lookpolymers.com All Rights Reserved